STUDI KOROSI ATMOSFERIK PADA BAJA PROFIL SIKU SNI 07-2054-2006 YANG DIPAPAR DALAM LINGKUNGAN FAKULTAS TEKNIK UNIVERSITAS SYIAH KUALA
Pengarang
RIAN JUNANDA BACHTIAR - Personal Name;
Dosen Pembimbing
Syarizal Fonna - 197810272008121001 - Dosen Pembimbing I
Sulaiman Thalib - 196102101990021001 - Dosen Pembimbing II
Nomor Pokok Mahasiswa
1604102010041
Fakultas & Prodi
Fakultas Teknik / Teknik Mesin (S1) / PDDIKTI : 21201
Subject
Kata Kunci
Penerbit
Banda Aceh : Fakultas Teknik - Teknik Mesin., 2022
Bahasa
No Classification
-
Literature Searching Service
Hard copy atau foto copy dari buku ini dapat diberikan dengan syarat ketentuan berlaku, jika berminat, silahkan hubungi via telegram (Chat Services LSS)
Korosi atmosfer adalah degradasi dan rusaknya bahan logam karena berinteraksi dengan atmosfer. Kerusakan akibat korosi atmosferik semakin parah dengan adanya polutan yang terkandung di udara. Penelitian ini bertujuan untuk mendapatkan laju korosi, mengkaji perkembangan inisiasi korosi dan perkembangan produk korosi atmosferik baja profil siku akibat pemaparan di lingkungan Fakultas Teknik Universitas Syiah Kuala, Darussalam, kota Banda Aceh, Provinsi Aceh Indonesia. Dalam penelitian ini menggunakan baja karbon yang berbentuk profil siku dengan ukuran dimensi 65 mm dengan ketebalan 6 mm (SNI 07-2054-2006). Waktu penelitian dilakukan selama empat bulan pemaparan, dimulai dari bulai februari sampai dengan bulai mei 2021. Perhitungan laju korosi menggunakan persamaan berdasarkan ASTM G-1. Hasil yang diperoleh dari empat bulan pemaparan didapatkan nilai laju korosi pada bulan februari yaitu 012255 mpy dan nilai laju korosi pada bulan mei yaitu 0,06466 mpy, sehingga tingkat ketahanan korosi relatif untuk baja profil siku dikategorikan menjadi outstanding (
Atmospheric corrosion is the degradation and destruction of metallic materials due to their interaction with the atmosphere. Damage due to atmospheric corrosion is getting worse with the presence of pollutants contained in the air. This study aims to obtain the corrosion rate, to study the development of corrosion initiation and the development of atmospheric corrosion products of elbow profile steel due to exposure in the Faculty of Engineering, Syiah Kuala University, Darussalam, Banda Aceh City, Aceh Province, Indonesia. In this study, carbon steel is used in the form of an angled profile with dimensions of 65 mm and a thickness of 6 mm (SNI 07-2054-2006). The research time was carried out for four months of exposure, starting from February to May 2021. Calculation of the corrosion rate using an equation based on ASTM G-1. The results obtained from four months of exposure showed that the corrosion rate value in February was 012255 mpy and the corrosion rate value in May was 0.06466 mpy, so the relative corrosion resistance level for elbow profile steel was categorized as outstanding (
STUDI PENGARUH KETEBALAN CAT TERHADAP LAJU KOROSI ATMOSFERIK (MUHAMMAD RAKIN, 2025)
STUDI LAJU KOROSI DAN PERKEMBANGAN PRODUK KOROSI ATMOSFERIK PADA BAJA PROFIL SIKU AKIBAT PEMAPARAN DI LINGKUNGAN FAKULTAS TEKNIK UNSYIAH (Muhibul Jamal, 2019)
STUDI EFEKTIVITAS BERBAGAI JENIS CAT SEBAGAI PELINDUNG KOROSI ATMOSFERIK BAGI BAJA PROFIL SIKU SNI 07-2054-2006 (Ila Niswatul Khaira, 2024)
ANALISA LAJU KOROSI ATMOSFERIK DI KAWASAN PEUKAN BADA ACEH BESAR DAN MEURAXA BANDA ACEH (Sudirman, 2023)
STUDI LAJU KOROSI ATMOSFERIK BAJA KONSTRUKSI DI LINGKUNGAN PABRIK KELAPA SAWIT (PKS) PTPN-I TANJUNG SEUMANTOH (RIZQI AULIA, 2019)