MEMBRAN SELULOSA ASETAT BERBAHAN DASAR LIMBAH TANDAN KOSONG KELAPA SAWIT TERMODIFIKASI SILIKA UNTUK HEMODIALISIS KREATININ
Pengarang
MIRZALISA - Personal Name;
Dosen Pembimbing
Nomor Pokok Mahasiswa
1808103010047
Fakultas & Prodi
Fakultas MIPA / Kimia (S1) / PDDIKTI : 47201
Subject
Kata Kunci
Penerbit
Banda Aceh : Fakultas MIPA Kimia., 2023
Bahasa
No Classification
-
Literature Searching Service
Hard copy atau foto copy dari buku ini dapat diberikan dengan syarat ketentuan berlaku, jika berminat, silahkan hubungi via telegram (Chat Services LSS)
ABSTRAK
Telah dilakukan penelitian membran selulosa asetat berbahan dasar limbah tandan kosong kelapa sawit yang dimodifika silika. Tujuan pembuatan membran ialah untuk membuktikan kinerja hemodialisis kreatinin. Karakterisasi membran dilakukan dengan menggunakan Scanning Electron Microscopy (SEM), X-Ray Diffraction (XRD), Differential Scanning Calorimetry (DSC), Thermogravimetric Analysis (TGA), dan Universal Testing Machine. Membran selulosa asetat murni (SA11%-Si0%) memiliki derajat pengembangan dan porositas sebesar 38,89% dan 21,23%, sedangkan membran yang dimodifikasi silika 40% (SA11%-Si40%) memiliki derajat pengembangan dan porositas yang lebih baik sebesar 41,44% dan 27,81%. Membran SA11%-Si0% memiliki nilai fluks sebesar 86,86 L/m2 jam, sedangkan membran SA11%-Si40% memiliki nilai fluks sebesar 96,25% L/m2 jam. Membran SA11%-Si0% mengadsorpsi kreatinin sebesar 3,102 mg/g sedangkan membran SA11%-Si40% dapat mengadsorpsi sebesar 8,242 mg/g dengan total removal kreatinin masing-masing membran 10,483 mg/g dan 10,062 mg/g. Membran termodifikasi silika 40% (SA11%-Si40%) memiliki kemampuan yang lebih baik dibandingkan membran murni (SA11%-Si0%) dalam proses hemodialisis kreatinin.
Kata kunci: Membran, selulosa asetat, silika, hemodialisis, kreatinin, adsorpsi
ABSTRACT A Research on cellulose acetate membranes made from TKKS modified by silica has been carried out. The purpose of making the membrane is to prove the performance of creatinine hemodialysis. Membrane characterization was carried out using Scanning Electron Microscopy (SEM), X-Ray Diffraction (XRD), Differential Scanning Calorimetry (DSC), Thermogravimetric Analysis (TGA), and Universal Testing Machine. The pure cellulose acetate membranes (SA11%-Si0%) had swelling and porosity degrees of 38.89% and 21.23%, while 40% silica modified membranes (SA11%-Si40%) had better swelling and the porosity degrees is 41.44% and 27.81%. The SA11%-Si0% membrane had a flux value of 86.86 L/m2 hour, while the SA11%-Si40% membrane had a flux value of 96.25% L/m2 hour. The SA11%-Si0% membrane adsorbed 3.102 mg/g of creatinine while the SA11%-Si40% membrane adsorbed 8.242 mg/g with a total removal of creatinine of 10.483 mg/g and 10.062 mg/g respectively. 40% silica modified membrane (SA11%-Si40%) has better performance than pure membrane (SA11%-Si0%) in creatinine hemodialysis process. Keywords: Membrane, cellulose acetate, silica, hemodialysis, creatinine, adsorption
MEMBRAN SELULOSA ASETAT BERBAHAN DASAR SELULOSA DARI LIMBAH TANDAN KOSONG KELAPA SAWIT YANG DIMODIFIKASI KARBON AKTIF UNTUK HEMODIALISIS KREATININ (ISRA YULVIANI, 2022)
MEMBRAN FORWARD OSMOSIS (FO) SELULOSA ASETAT DARI LIMBAH TANDAN KOSONG KELAPA SAWIT UNTUK DESALINASI AIR PAYAU (Sharmila Hasina, 2022)
MEMBRAN SELULOSA ASETAT TERMODIFIKASI KARBON AKTIF DARI LIMBAH PLASTIK POLIETILENA TEREFTALAT (PET) UNTUK PENGHILANGAN UREA DAN KREATININ DALAM LIMBAH DIALISAT SIMULASI (Mirzalisa, 2026)
PREPARASI DAN KARAKTERISASI MEMBRAN SELULOSA ASETAT TERGRAFTING GLISIDIL METAKHRILAT UNTUK PENGHILANGAN UREA DALAM CAIRAN DIALISAT (FAHRAIN FAHIRA, 2025)
PREPARASI DAN KARAKTERISASI MEMBRAN SELULOSA ASETAT TERMODIFIKASI SILIKA UNTUK PENGHILANGAN UREA DALAM AIR DIALISAT ARTIFISIAL (CUT NURUL MAGFIRAH, 2024)