Electronic Theses and Dissertation

Kelebihan kadar fosfat di perairan menyebabkan eutrofikasi (kondisi perairan dengan warna air kehijauan atau keruh) dan terjadinya blooming fitoplankton yang menyebabkan kematian berbagai jenis biota perairan. Salah satu upaya untuk meminimalisir dampak fosfat adalah metode adsorpsi. Cangkang tiram adalah salah satu adsorben yang dapat digunakan karena mengandung 80-95% CaCO3 yang menunjukkan kadar mineral atau abu yang tinggi. Dalam penelitian ini cangkang tiram sebanyak 3 kg yang diperoleh dari Gampong Tibang dibersihkan dan dijemur di bawah sinar matahari. Selanjutnya cangkang tiram dihaluskan hingga diperoleh serbuk cangkang tiram yang telah lolos ayakan 100 mesh sebanyak 742,5 g. Kemudian serbuk cangkang tiram dikeringkan menggunakan oven pada suhu 105oC hingga berat serbuk konstan. Selanjutnya cangkang tiram dikalsinasi menggunakan furnace pada suhu 900oC selama 4 jam untuk menghasilkan abu cangkang tiram (adsorben CaO). Kemudian adsorben tersebut dikarakterisasi menggunakan XRD dan SEM. Hasil uji SEM menunjukkan banyak pori-pori yang terbentuk dengan luas permukaan rata-rata pori adsorben adalah 9,9 μm. Hasil uji XRD menunjukkan bahwa atom-atom tersusun secara teratur dan memiliki bentuk kristal. Adsorben abu cangkang tiram diuji penyerapannya terhadap fosfat dalam larutan berair dan diperoleh kondisi optimum terjadi pada pH 5, waktu kontak 55 menit, massa adsorben 0,1 g dan konsentrasi 210 mg/L. Pengujian isoterm adsorpsi dilakukan menggunakan isoterm Langmuir dan Freundlich, dari kedua jenis isoterm tersebut yang paling sesuai dengan proses adsorpsi fosfat menggunakan adsorben abu cangkang tiram adalah isoterm Freundlich dengan nilai R2 yaitu 0,981.

Excess levels of phosphate in the waters cause eutrophication (water conditions with greenish or cloudy water color) and phytoplankton blooms that cause the death of various types of aquatic biota. One of the efforts to minimize the impact of phosphate is the adsorption method. Oyster shell is one of the adsorbents that can be used because it contains 80-95% CaCO3 which indicates high mineral or ash content. In this study, 3 kg of oyster shells obtained from the village of Tibang were cleaned and dried in the sun. Furthermore, the oyster shells were mashed to obtain 742.5 g of oyster shell powder that had passed a 100 mesh sieve. Then the oyster shell powder was dried using an oven at a temperature of 105oC until the powder weight was constant. Furthermore, oyster shells were calcined using a furnace at a temperature of 900oC for 4 hours to produce oyster shell ash (CaO adsorbent). Then the adsorbent was characterized using XRD and SEM. The results of the SEM test showed that many pores were formed with the average surface area of ​​the adsorbent being 9.9 m. XRD test results show that the atoms are arranged in an orderly manner and have a crystalline form. The oyster shell ash adsorbent was tested for its absorption of phosphate in aqueous solution and the optimum condition was found at pH 5, contact time 55 minutes, adsorbent mass 0.1 g and concentration 210 mg/L. The adsorption isotherm test was carried out using Langmuir and Freundlich isotherms, of the two types of isotherms the most suitable for the phosphate adsorption process using oyster shell ash adsorbent was the Freundlich isotherm with an R2 value of 0.981.