PEMBUATAN KOMPOSIT KITOSAN MAGNETIK TERSULFONASI BERIKATAN SILANG GLUTARALDEHID SEBAGAI ADSORBEN MERKURI
Pengarang
ANGGUN S W A - Personal Name;
Dosen Pembimbing
Nomor Pokok Mahasiswa
1508103010055
Fakultas & Prodi
Fakultas MIPA / Kimia (S1) / PDDIKTI : 47201
Subject
Kata Kunci
Penerbit
Banda Aceh : Universitas Syiah Kuala., 2019
Bahasa
Indonesia
No Classification
-
Literature Searching Service
Hard copy atau foto copy dari buku ini dapat diberikan dengan syarat ketentuan berlaku, jika berminat, silahkan hubungi via telegram (Chat Services LSS)
ABSTRAK
Pembuatan komposit kitosan magnetik tersulfonasi berikatan silang glutaraldehid (K-BM-S-GLA) telah berhasil dilakukan dan diaplikasikan sebagai adsorben merkuri. Pembuatan komposit K-BM-S-GLA dilakukan dengan variasi komposisi kitosan tersulfonasi, pasir besi dan glutaraldehid (GLA). Pasir besi diperoleh dari pantai Syiah Kuala, Banda Aceh. Komposit K-BM-S-GLA dikarakterisasi menggunakan Fourier Transform Infrared (FT-IR), X-Ray Diffraction (XRD) dan Scanning Electron Microscope (SEM). Komposisi terbaik dari komposit K-BM-S-GLA yaitu 0,65 g kitosan tersulfonasi, 0,5 g pasir besi dan GLA 0,17 M. Hasil uji adsorpsi menunjukkan bahwa kapasitas adsorpsi tertinggi diperoleh pada waktu kontak 60 menit dan pH 3. Adsorpsi merkuri menggunakan komposit K-BM-S-GLA mengikuti model isoterm adsorpsi Langmuir dan Freundlich. Kapasitas adsorpsi maksimum berdasarkan isoterm adsorpsi Langmuir adalah 93,46 mg/g. Aplikasi adsorben pada limbah pertambangan emas menunjukkan persen penghilangan merkuri mencapai 98,24%.
Kata kunci: glutaraldehid, kitosan, merkuri, pasir besi, sulfonasi
ABSTRACT
Preparation of glutaraldehyde crosslinked sulfonated magnetic chitosan composite (K-BM-S-GLA) has been successfully conducted and applied as an adsorbent of mercury. K-BM-S-GLA composites were prepared with various composition of sulfonated chitosan, iron sand, and glutaraldehyde (GLA). Iron sand was obtained from Syiah Kuala beach, Banda Aceh. K-BM-S-GLA composites were characterized using Fourier Transform Infrared (FT-IR), X-Ray Diffraction (XRD) and Scanning Electron Microscope (SEM). The best composition of K-BM-S-GLA composites was 0.65 g sulfonated chitosan, 0.5 g iron sand and GLA 0.17 M. Based on adsorption study, the highest adsorption capacity was obtained at the contact time of 60 minutes and pH 3. Mercury adsorption by the K-BM-S-GLA composites fitted to both Langmuir and Freundlich adsorption isotherm models. The maximum adsorption capacity based on Langmuir's adsorption isotherm was 93.46 mg/g. The application of adsorbent in the gold mining waste showed the percentage of mercury removal was reached 98.24%.
Keywords: chitosan, glutaraldehyde, iron sand, mercury, sulfonation
Tidak Tersedia Deskripsi
PEMBUATAN KOMPOSIT KITOSAN MAGNETIK TERSULFONASI BERIKATAN SILANG GLUTARALDEHID SEBAGAI ADSORBEN MERKURI (ANGGUN S W A, 2019)
MODIFIKASI KITOSAN MENGGUNAKAN PASIR BESI DAN GLUTARALDEHID SERTA APLIKASINYA SEBAGAI ADSORBEN LIMBAH MERKURI DI PERTAMBANGAN EMAS MANGGAMAT, ACEH (FITRI PURNAMA WATI, 2018)
MODIFIKASI KITOSAN MENGGUNAKAN PASIR BESI, PENGIKAT SILANG PEGDE DAN HIDROLISAT PROTEIN DARI BIJI PETAI CINA SEBAGAI ADSORBEN ION LOGAM KADMIUM (CUT PUTRI AULIA, 2020)
PEMBUATAN DAN KARAKTERISASI KOMPOSIT KITOSAN MAGNETIK BERIKATAN SILANG H2SO4 DAN APLIKASINYA SEBAGAI ADSORBEN METHYLENE BLUE (ISHMATURRAHMI, 2018)
PEMBUATAN KOMPOSIT KITOSAN-ASPARAGIN MAGNETIK BERIKAT SILANG PEDGE DAN APLIKASINYA SEBAGAI ADSORBEN METHYLENE BLUE (MUTAWALLY, 2023)