SINTESA SILIKA DOPING ALUMINIUM DENGAN METODE SOL GEL SEBAGAI MATERIAL THERMOLUMINESCENCE DOSIMETER (TLD)
Pengarang
Nurul Azmi - Personal Name;
Dosen Pembimbing
Nomor Pokok Mahasiswa
0908102010030
Fakultas & Prodi
Fakultas MIPA / Fisika (S1) / PDDIKTI : 45201
Subject
Kata Kunci
Penerbit
Banda Aceh : Fakultas Matematika dan Ilmu Pengetahuan Alam., 2014
Bahasa
Indonesia
No Classification
546.673
Literature Searching Service
Hard copy atau foto copy dari buku ini dapat diberikan dengan syarat ketentuan berlaku, jika berminat, silahkan hubungi via telegram (Chat Services LSS)
ABSTRAK
Telah dilakukan sintesa silika doping aluminium (SiO2:Al) dengan metode sol gel sebagai salah satu material TLD. Penelitian ini bertujuan untuk melakukan sintesa material TLD dari bahan SiO2:Al dan menguji pengaruh dari konsentrasi doping Al terhadap struktur kristal, morfologi permukaan, dan sifat optik dari material tersebut. Konsentrasi Al divariasikan dari 0% mol, 0.1% mol, dan 2% mol. Hasil dari pencampuran dimasukkan ke dalam cetakan berbentuk cakram yang tebalnya 1 mm dan diameter 2 cm dan 8 mm. Sampel gel kering yang diperoleh selanjutnya di sintering pada suhu 350??, 500??, dan 830??. Kemudian sampel SiO2:Al di karakterisasi dengan menggunakan XRD, SEM/EDS, dan spektrometer UV-Vis. Hasil penelitian menunjukkan bahwa struktur SiO2 yang berbentuk amorf, namun setelah didoping dengan Al2O3 strukturnya menjadi kristalbolik. Ukuran Kristal SiO2:Al terbesar adalah 9.24 nm. Morfologi permukaan SiO2:Al, dengan pendopingan Al yang dihasilkan homogen. Celah pita energi terkecil 2.86 eV untuk SiO2 yang didoping Al. Berdasarkan karakteristik dari bahan tersebut dapat disimpulkan bahwa, silika doping aluminium dapat digunakan sebagai TLD.
Kata Kunci : SiO2:Al, Sol gel, struktur Kristal, ukuran Kristal, morfologi permukaan, celah pita optik.
?
ABSTRACT
Synthesis of aluminum doped silica (SiO2:Al) as a TLD material using sol gel method have seen investigated. The aim of this study is to synthesize material of TLD SiO2:Al and examine the effects of Al doped concentration on the crystal structure, surface morphology, and optical properties of these materials. Concentration of Al was varied from 0% mol, 0.1% mol, and 2% mol. The results of the solution was poured into the disc-shape mould which its thickness of 1 mm and its diameter of 2 cm and 8 mm. The samples of dried gel were then sintering at the 350??, 500??, and 830??. Then, the SiO2:Al samples were characterized by using XRD, SEM/EDX, and UV-Vis spectrometer. The results showed that the SiO2 sample has amorphous structure, but after doped with Al2O3 the structure become cristabolite. The greatest crystal size of SiO2:Al is 9.24 nm. The morphology of surface of SiO2:Al, homogeneous found for sample was Al2O3 doped. The smallest band gap energy 2.86 eV was doped Al for SiO2. These results can be concluded that this material have a good potential for TLD application.
Keywords: SiO2:Al, Sol gel, crystal structure, crystal size, surface morphology, optical band gap.
Tidak Tersedia Deskripsi
SINTESA FOTOELEKTRODA TIO2 CO-DOPING MG/LA UNTUK APLIKASI DYE SENSITIZED SOLAR CELL (DSSC) (NURUL AZMI, 2020)
PENGARUH KOMPOSISI REFRAKTORI DOLOMIT ALUMINIUM SILIKA ANTARA IKATAN TANAH LIAT DAN TAR TERHADAP KUAT TEKAN (ZULFAN YAHYA, 2023)
ANALISIS SIFAT MEKANIS DAN SIFAT FISIS ALUMINIUM BEKAS HASIL CORAN (Tio Muger Stiawan, 2015)
KAJI EKSPERIMENTAL PENGARUH PERBANDINGAN UDARA DAN BAHAN BAKAR GAS (ASETILIN) TERHADAP TEMPERATUR API PADA DAPUR PELEBURAN LOGAM (Muhammad Arief, 2018)
UPAYA PENCEGAHAN PENGGUNAAN DOPING PADA ATLET CABANG OLAHRAGA ANGKAT BESI BINAAN KONI ACEH TAHUN 2019 (Fiki Eduansah, 2020)