Anna Fitria Rossa Primary Author mixed material bibliography Banda Aceh Universitas Syiah Kuala 2016 id Indonesia

Null

ABSTRAK Nama : Anna Fitria Rossa Program Studi : Kedokteran Gigi Judul : Pengaruh Penggodokan Terhadap Monomer Sisa pada Elemen Gigi Tiruan Resin Akrilik. Gigi tiruan resin akrilik terdiri dari basis dan elemen gigi tiruan. Elemen gigi tiruan yang paling sering digunakan adalah elemen gigi tiruan resin akrilik. Pada prosedur pembuatan gigi tiruan diperlukan proses polimerisasi dimana ikatan kimiawi antara elemen gigi tiruan dan basis terjadi melalui proses polimerisasi. Resin akrilik heat-cured dipolimerisasi menggunakan pemanasan air (penggodokan). Meskipun berbagai metode digunakan untuk memulai reaksi polimerisasi namun konversi monomer menjadi polimer tidak pernah sempurna dan selalu terdapat monomer yang tidak habis bereaksi (monomer sisa). Adanya monomer sisa pada resin akrilik berpotensi menyebabkan iritasi, peradangan, dan reaksi alergi pada mukosa mulut. Penelitian ini bertujuan untuk melihat jumlah monomer sisa pada elemen gigi tiruan resin akrilik setelah dilakukan penggodokan. Penelitian ini menggunakan elemen gigi tiruan resin akrilik merk GC Permacryl China dan Basic. Spesimen berjumlah 12 spesimen dari 2 merk yang berbeda. Spesimen dari setiap merk di bagi menjadi 3 spesimen yang dilakukan penggodokan dan 3 spesimen tidak dilakukan penggodokan. Pengukuran monomer sisa menggunakan Gas Kromatografi dengan jenis detektor Flame Ionization Detector (FID). Analisis statistik pada penelitian ini menggunakan uji t-test independent. Hasil uji t-test independent menunjukkan bahwa tidak ada perbedaan yang bermakna (p>0.05) antara elemen gigi tiruan resin akrilik merk GC Permacryl China dan Basic yang dilakukan pengodokan dan tanpa penggodokan. Dapat disimpulkan bahwa tidak terdapat pengaruh penggodokan terhadap monomer sisa elemen gigi tiruan resin akrilik dan tidak terdapat perbedaan jumlah monomer sisa antara elemen gigi tiruan resin akrilik merk GC Permacryl China dan dan merk Basic. Kata Kunci : Elemen gigi tiruan resin akrilik, monomer sisa, penggodokan, gas kromatografi flame ionization detector ABSTRACT Name : Anna Fitria Rossa Program Study : Dentistry Title : The Effect of Curing to Residual Monomer on Resin Acrylic Artificial teeth Resin acrylic prosthesis consist of denture base and artificial teeth. The most common use of artificial teeth is from resin acrylic. One of step in procedure to make a prosthesis is polymerization which chemical bound between artificial teeth and denture base occur with polymerization. Resin acrylic heat cured was polymerized using wet heat (curing). Although many methods was used in polymerization but the conversion of monomer to be polymer never be completed and always conduct of residual monomer. The residual monomer of resin acrylic could lead to irritation, inflammation and allergic reaction of oral mucous. This study was aimed to analyze the effect of residual monomer on resin acrylic artificial teeth after curing. This study was using resin acrylic artificial teeth GC Permacryl China and Basic. Specimens was 12 from different brands. Specimens of each brand was divided into 2 groups which consist of 3 specimens. 3 specimens was curing and the others without curing. The measuring of residual monomer was using gas chromatography with Flame Ionization Detector (FID) system. The data of this study was analyzed using t-test independent. The result shown that there was no significant different (p > 0,05) between artificial teeth of Permacryl and Basic with curing and without curing. It can be concluded that there was no effect of curing to residual monomer of resin acrylic artificial teeth Permacryl and Basic brands. Keywords: Resin acrylic artificial teeth, residual monomer, curing, gas chromatography FID 0 ELECTRONIC THESES AND DISSERTATION Universitas Syiah Kuala 24987 2016-08-27 13:11:40 2016-08-29 09:47:10 machine generated