Electronic Theses and Dissertation

Penelitian ini bertujuan untuk mengevaluasi efektivitas ekstrak etanol daun ubi jalar (Ipomoea batatas L.) sebagai inhibitor korosi pada pelat baja tahan karat 304 SS dalam media asam (HCl 1 M), basa (NaOH 1 M), dan garam (NaCl 3,5%). Laju korosi ditentukan menggunakan metode kehilangan massa (weight loss), sedangkan karakterisasi ekstrak dilakukan melalui uji fitokimia, penentuan Total Phenolic Content (TPC), Total Flavonoid Content (TFC), dan Fourier Transform Infrared Spectroscopy (FTIR). Hasil uji fitokimia menunjukkan bahwa ekstrak etanol daun ubi jalar mengandung senyawa alkaloid, flavonoid, fenolik, dan saponin. Penetapan kandungan metabolit sekunder menghasilkan nilai TPC sebesar 47,09 ± 0,30 mg GAE/g dan TFC sebesar 9,43 ± 1,43 mg QE/g, yang menunjukkan tingginya kandungan senyawa bioaktif yang berpotensi berperan dalam mekanisme inhibisi korosi. Analisis FTIR mengidentifikasi keberadaan gugus fungsi O–H, C–H alifatik, C=C aromatik, C=O ester, dan C–O–C eter yang mengindikasikan adanya senyawa metabolit sekunder sebagai penyusun lapisan pelindung pada permukaan logam. Hasil pengujian menunjukkan bahwa kondisi optimum penghambatan korosi pada media HCl diperoleh pada konsentrasi inhibitor 600 ppm dengan laju korosi rata-rata sebesar 0,1 mmpy dan efisiensi inhibisi sebesar 90%. Pada media NaOH, kondisi optimum dicapai pada konsentrasi 900 ppm dengan laju korosi rata-rata sebesar 0,08 mmpy dan efisiensi inhibisi sebesar 75%, sedangkan pada media NaCl 3,5% kondisi optimum diperoleh pada konsentrasi 900 ppm dengan laju korosi rata-rata sebesar 0,089 mmpy dan efisiensi inhibisi sebesar 85%. Pengamatan morfologi permukaan pelat baja menggunakan USB Digital Microscope pada pembesaran 100× menunjukkan bahwa penambahan ekstrak etanol daun ubi jalar mampu mengurangi pembentukan produk korosi melalui pembentukan lapisan pelindung pada permukaan logam. Dengan demikian, ekstrak etanol daun ubi jalar berpotensi sebagai inhibitor korosi alami yang efektif untuk meningkatkan ketahanan korosi pelat baja tahan karat 304 SS, terutama dalam media HCl.

Kata kunci: ekstrak etanol ubi jalar, pelat baja 304 SS, inhibitor korosi, larutan HCl 1M, NaOH 1M, dan NaCl 3,5%.

This study aimed to evaluate the effectiveness of sweet potato (Ipomoea batatas L.) leaf ethanol extract as a corrosion inhibitor for 304 stainless steel (304 SS) plates in acidic ( HCl 1M), alkaline (NaOH 1M), and saline ( NaCl 3,5%) media. The corrosion rate was determined using the weight loss method, while the extract was characterized through phytochemical screening, determination of Total Phenolic Content (TPC), Total Flavonoid Content (TFC), and Fourier Transform Infrared Spectroscopy (FTIR). Phytochemical analysis confirmed the presence of alkaloids, flavonoids, phenolics, and saponins. The extract exhibited a TPC value of 47.09 ± 0.30 mg GAE/g and a TFC value of 9.43 ± 1.43 mg QE/g, indicating a high content of bioactive compounds with potential corrosion inhibition properties. FTIR analysis identified the presence of O–H, aliphatic C–H, aromatic C=C, ester C=O, and ether C–O–C functional groups, suggesting the presence of secondary metabolites capable of forming a protective layer on the metal surface. The optimum corrosion inhibition in the acidic medium was achieved at an inhibitor concentration of 600 ppm, resulting in an average corrosion rate of 0.1 mmpy and an inhibition efficiency of 90%. In the alkaline medium, the optimum condition was obtained at 900 ppm, with an average corrosion rate of 0.08 mmpy and an inhibition efficiency of 75%, while in the saline medium, the optimum performance was also achieved at 900 ppm, yielding an average corrosion rate of 0.089 mmpy and an inhibition efficiency of 85%. Surface morphology observations using a USB Digital Microscope at 100× magnification revealed that the addition of sweet potato leaf ethanol extract reduced corrosion product formation by promoting the formation of a protective film on the metal surface. These findings demonstrate that sweet potato leaf ethanol extract has significant potential as a natural corrosion inhibitor for enhancing the corrosion resistance of 304 stainless steel, particularly in acidic media. Keywords: sweet potato ethanol extract, 304 SS steel plate, corrosion inhibitor, acid, base, and salt solutions.