PENGGUNAAN BAKTERI BACILLUS SP. UNTUKRNPERBAIKAN RETAK DENGAN METODE INJEKSI PADARNPELAT BETON BERTULANG MUTU TINGGI 85 MPA YANGRNMENGALAMI GAGAL IMPACT
Pengarang
REGA ADYATMA SULUBERE - Personal Name;
Dosen Pembimbing
Teuku Budi Aulia - 196705291994031001 - Dosen Pembimbing I
Purwandy Hasibuan - 198210182006041001 - Dosen Pembimbing I
Nomor Pokok Mahasiswa
2104101010148
Fakultas & Prodi
Fakultas Teknik / Teknik Sipil (S1) / PDDIKTI : 22201
Subject
Kata Kunci
Penerbit
Banda Aceh : Fakultas Teknik Sipil., 2026
Bahasa
No Classification
-
Literature Searching Service
Hard copy atau foto copy dari buku ini dapat diberikan dengan syarat ketentuan berlaku, jika berminat, silahkan hubungi via telegram (Chat Services LSS)
Beton bertulang mutu tinggi memiliki kuat tekan tinggi, namun tetap rentan
mengalami retak akibat beban impact yang dapat menurunkan kinerja struktur.
Penelitian ini bertujuan menganalisis perilaku pelat beton bertulang mutu tinggi
setelah mengalami kerusakan akibat beban impact serta mengevaluasi efektivitas
injeksi bakteri Bacillus sp. sebagai self-healing agent. Penelitian menggunakan
pelat beton bertulang mutu 85 MPa dengan variasi dimensi 40×40×5 cm, 60×60×5
cm, dan 80×80×5 cm. Injeksi dilakukan menggunakan larutan bakteri Bacillus sp.
berkonsentrasi 0,6%, kemudian dilakukan pengujian impact dengan parameter
jumlah pukulan, energi serapan, regangan, dan pola retak. Hasil penelitian
menunjukkan bahwa injeksi bakteri mampu mempertahankan kapasitas benturan
pelat beton hingga 70% setelah mengalami kerusakan. Kapasitas impact pelat
setelah injeksi meningkat dibandingkan pelat tanpa injeksi, sedangkan pelat dengan
aspek rasio yang lebih kecil memiliki kemampuan menahan benturan lebih tinggi.
Aktivitas bakteri yang menghasilkan endapan kalsium karbonat (CaCO₃)
membantu mengisi retakan sehingga memperlambat perkembangan retak dan
meningkatkan ketahanan pelat beton terhadap beban impact.
High-strength reinforced concrete possesses high compressive strength and durability; however, it remains susceptible to cracking under impact loading, which can reduce its structural performance. This study aims to analyze the behavior of high-strength reinforced concrete slabs after impact-induced damage and to evaluate the effectiveness of Bacillus sp. injection as a self-healing agent. The study used 85 MPa reinforced concrete slabs with dimensions of 40 × 40 × 5 cm, 60 × 60 × 5 cm, and 80 × 80 × 5 cm. The cracks were repaired by injecting a 0.6% Bacillus sp. solution, followed by impact testing to evaluate the number of blows, absorbed energy, strain, and crack patterns. The results indicate that bacterial injection was able to maintain up to 70% of the impact resistance of the damaged concrete slabs. The impact capacity of the repaired slabs increased compared to unrepaired specimens, while slabs with lower aspect ratios exhibited greater impact resistance. The precipitation of calcium carbonate (CaCO₃) produced by the bacterial activity effectively filled the cracks, slowed crack propagation, and improved the slabs' resistance to impact loading.
PENGGUNAAN BAKTERI BACILLUS SP.UNTUK PERBAIKAN STRUKTUR DENGAN METODE INJEKSI PADA PLAT BETON BERTULANG MUTU TINGGI 85 MPA YANG MENGALAMI GAGAL IMPACT. (Arivandi, 2026)
PENGGUNAAN BAKTERI BACILLUS SP. UNTUK PERBAIKAN STRUKTUR BALOK BETON BERTULANG YANG MENGALAMI KEGAGALAN LENTUR DENGAN METODE INJEKSI (FARAS DWI PUTRA, 2025)
PERBAIKAN BALOK BETON BERTULANG MUTU TINGGI TERHADAPRNKEGAGALAN GESER MELALUI METODE INJEKSI BAKTERI BACILUS SP. (Riski Armianda, 2026)
EFEKTIFITAS PERBAIKAN BALOK BETON BERTULANG MUTU TINGGI YANG MENGALAMI KEGAGALAN LENTUR MENGGUNAKAN BAKTERI BACILLUS SP. SECARA INTERNAL DAN EKTERNAL (FARAS DWI PUTRA, 2026)
ANALISIS PERILAKU LENTUR PADA BALOK BETON BERTULANG MUTU TINGGI SETELAH RETAK YANG DIPERBAIKI DENGAN INJEKSI EPOXY (Fiany Fajar Puspita, 2017)