Sintesis dan karakterisasi turunan basa Schiff dari p-hidroksibenzaldehida dan anilin sebagai inhibitor korosi pada baja karbon dalam larutan asam klorida telah dilakukan. Senyawa basa Schiff yang dihasilkan berupa N-(4-hidroksibenzilidena) anilin dengan rendemen sebesar 98%, berbentuk padatan putih kekuningan, dan memiliki titik lebur 197 °C. Hasil karakterisasi menggunakan Kromatografi Lapis Tipis (KLT) menunjukkan dua noda dengan nilai Rf 0,64 pada eluen 9:1 (lebih nonpolar) dan Rf 0,53 pada eluen 1:9 (lebih polar). Spektrum Fourier Transform Infrared (FTIR) memperlihatkan pita serapan khas gugus imina C=N pada bilangan gelombang 1583 cm⁻¹. Karakterisasi menggunakan Spektroskopi Resonansi Magnet Inti Proton (¹H-NMR) menunjukkan sinyal khas proton imina C=N pada pergeseran kimia 8,5 ppm, sedangkan Spektroskopi Resonansi Magnet Inti Karbon (¹³C-NMR) menampilkan sinyal karbon imina pada pergeseran kimia 159 ppm. Uji aktivitas inhibitor korosi menggunakan metode Electrochemical Impedance Spectroscopy (EIS) menunjukkan efisiensi inhibisi tertinggi sebesar 79% pada konsentrasi 0,01 M, sedangkan metode polarisasi potensiodinamik menghasilkan efisiensi inhibisi tertinggi sebesar 98,8% pada konsentrasi yang sama. Hasil ini menunjukkan bahwa senyawa basa Schiff yang disintesis berpotensi sebagai inhibitor korosi yang efektif pada baja karbon dalam larutan asam klorida.

Kata kunci : Basa Schiff, baja karbon, korosi, inhibitor korosi, media asam

The synthesis and characterization of Schiff base derivatives from p-hydroxybenzaldehyde and aniline as corrosion inhibitors for carbon steel in hydrochloric acid solution have been carried out. The synthesized Schiff base, N-(4-hydroxybenzylidene) aniline, was obtained with a yield of 98%, appeared as a yellowish-white solid, and had a melting point of 197 °C. Characterization using Thin Layer Chromatography (TLC) showed two spots with Rf values of 0.64 in a 9:1 eluent system (more nonpolar) and 0.53 in a 1:9 eluent system (more polar). The Fourier Transform Infrared (FTIR) spectrum exhibited a characteristic absorption band of the imine C=N group at 1583 cm⁻¹. Characterization using Proton Nuclear Magnetic Resonance (¹H-NMR) revealed a characteristic signal of the imine proton C=N at a chemical shift of 8.5 ppm, while Carbon-13 Nuclear Magnetic Resonance (¹³C-NMR) showed the imine carbon signal at a chemical shift of 159 ppm. The corrosion inhibition activity evaluated using Electrochemical Impedance Spectroscopy (EIS) showed the highest inhibition efficiency of 79% at a concentration of 0.01 M, whereas the potentiodynamic polarization method exhibited the highest inhibition efficiency of 98.8% at the same concentration. These results indicate that the synthesized Schiff base has strong potential as an effective corrosion inhibitor for carbon steel in hydrochloric acid solution. Keywords: Schiff base, carbon steel, corrosion, corrosion inhibitor, acid media