Penelitian ini bertujuan untuk mengetahui perbandingan ketahanan korosi beton bertulang normal (BBNOR) dengan beton bertulang substitusi 5% persentase sebagian semen menggunakan abu pozzolan (BBPOZ), abu sekam padi (BBASP), dan abu tempurung kelapa (BBATK). Benda uji berupa balok beton FAS 0,50 dengan f’c 25 MPa dan berukuran 10×10×30 cm bertulangan tunggal BjTS 280 diameter 10 mm. Variasi beton diuji dalam dua perlakuan berbeda, yaitu perendaman air tanah bersalinitas tawar dengan metode submersion secara alamiah dan perendaman NaCl 3,5% dengan metode wet - dry cycle selama 54 minggu. Nilai potensial korosi diukur menggunakan metode half - cell potential mapping serta nilai pH beton diukur menggunakan metode ASTM F710 dan metode ESL (Ex – Situ Leaching). Hasil nilai potensial korosi dan nilai pH beton dianalisis berdasarkan diagram pourbaix untuk mengetahui fase korosi yang terjadi. Berdasarkan hasil nilai potensial korosi dan fase korosi yang terjadi pada setiap variasi beton maka urutan ketahanan korosi dari yang tertinggi hingga terendah dari kedua perlakuan media rendaman adalah BBASP, BBPOZ, BBATK, dan BBNOR. Penggunaan material pozzolanik terbukti meningkatkan ketahanan korosi jangka panjang melalui reaksi hidrasi sekunder yang membentuk tambahan senyawa C-S-H. Hasil ini menunjukkan bahwa pemanfaatan material pozzolanik berbasis limbah lokal sebagai substitusi sebagian semen dapat menjadi alternatif ramah lingkungan untuk mendukung konstruksi berkelanjutan.

This study aims to compare the corrosion resistance of normal reinforced concrete (BBNOR) with reinforced concrete in which 5% of the cement is partially substituted using pozzolan ash (BBPOZ), rice husk ash (BBASP), and coconut shell ash (BBATK). The test specimens were concrete beams with a water cement ratio of 0,50 a compressive strength of 25 Mpa and dimension of 10×10×30 cm reinforced with a single BjTS 280 steel bar of 10 mm diameter. The concrete variations were tested under two different conditions, immersion in freshwater ground water using natural submersion and immersion in 3,5% NaCl solution using a wet - dry cycle for 54 weeks. Corrosion potential was measured using the half - cell potential mapping method, while concrete pH was measured using the ASTM F710 and ESL (Ex - Situ Leaching) methods. The corrosion phase was determined by analyzing the corrosion potential and pH values using the pourbaix diagram. Based on the results of the corrosion potential values and corrosion phases that occur in each concrete variation, the order of corrosion resistance from highest to lowest of the two immersion media treatment are BBASP, BBPOZ, BBATK, and BBNOR. The use of pozzolanic materials has proven to enhance long term corrosion resistance through secondary hydration reactions that produce additional C-S-H compounds. These results indicate that utilizing locally sourced pozzolanic waste materials as partial cement substitutes can be an environmentally friendly alternative to support sustainable construction.