PREPARASI DAN KARAKTERISASI BEADS NANOKOMPOSIT KITOSAN/TIO2 DAN APLIKASINYA PADA PENGHILANGAN ZAT WARNA RHODAMIN B
Pengarang
CANTIK ORIZA SIREGAR - Personal Name;
Dosen Pembimbing
Surya Lubis - 196905101999032001 - Dosen Pembimbing I
Nomor Pokok Mahasiswa
2008103010062
Fakultas & Prodi
Fakultas MIPA / Kimia (S1) / PDDIKTI : 47201
Subject
Penerbit
Banda Aceh : Fakultas MIPA Kimia., 2025
Bahasa
Indonesia
No Classification
572.45
Literature Searching Service
Hard copy atau foto copy dari buku ini dapat diberikan dengan syarat ketentuan berlaku, jika berminat, silahkan hubungi via telegram (Chat Services LSS)
ABSTRAK
Green synthesis nanopartikel titanium dioksida (TiO2) dan modifikasinya dengan
kitosan menghasilkan beads nanokomposit kitosan/TiO2 telah berhasil dilakukan.
Nanopartikel TiO2 disintesis dari prekursor titanium tetraisopropoksida
menggunakan ekstrak etanol kulit buah alpukat yang mengandung senyawa
metabolit sekunder yang berperan sebagai bioreduktor, stabilisator dan capping
agent dalam proses sintesis nanopartikel TiO2. Kandungan Total Phenolic Content
(TPC) dan Total Flavonoid Content (TFC) ekstrak etanol kulit buah alpukat adalah
79,75 mg GAE/g dan 21,74 mg QE/g. Nanokomposit kitosan/TiO2 dipreparasi
dalam bentuk beads dengan perbandingan kitosan terhadap TiO2 (b/b) yaitu 1:1. 1:2
dan 2:1. Karakterisasi material yang dihasilkan dilakukan menggunakan instrumen
Difraksi sinar-X, spektroskopi Fourier transform Inframerah, Scanning Electron
Microscopy-Energy-Dispersive X-Ray Spectroscopy (SEM-EDX), Diffuse
Reflectance Spectroscopy (UV-Vis DRS) dan Brunauer Emmett Teller (BET).
Nanopartikel TiO2 yang diperoleh memiliki fasa anatase dan rutil dengan ukuran
kristal rata-rata 19,28 nm dan partikel berbentuk bulat (sferis). Beads nanokomposit
kitosan/TiO2 dengan perbandingan 1:1. 1:2 dan 2:1 memiliki rata-rata ukuran kristal
yang lebih kecil dibandingkan dengan nanopartikel TiO2 yaitu berturut-turut: 14,49
nm; 11,21 nm; dan 9,41 nm. Selain itu, beads nanokomposit kitosan/TiO2 1: 1 juga
memiliki energi celah pita yang lebih kecil (3,21 eV) dibandingkan dengan
nanopartikel TiO2 (3,26 eV). Hasil uji aktivitas fotokatalitik pada penghilangan zat
warna rhodamin B (RhB) menunjukkan beads nanokomposit kitosan/TiO2 1:1
memiliki aktivitas fotokatalitik yang lebih tinggi dibandingkan beads
nanokomposit kitosan/TiO2 1:2, dan 2:1. Beads nanokomposit kitosan/TiO2 1:1
mampu menghilangkan zat warna RhB hingga 52,74% setelah diiradiasi dengan
sinar ultra violet dan 94,98% setelah diiradiasi dengan sinar matahari selama 120
menit pada kondisi optimum pH awal larutan RhB yaitu 11, massa fotokatalis 300
mg dan konsentrasi RhB awal sebesar 1 ppm.
Kata Kunci: Biosintesis, fotokatalis, beads, kitosan/TiO2, rhodamin B
ABSTRACT Green synthesis of titanium dioxide nanoparticles (TiO2 NPs) and their modification with chitosan to produce chitosan/TiO2 nanocomposite beads has been successfully carried out. TiO2 NPs were synthesized from titanium tetraisopropoxide using the ethanol extract of avocado fruit peel that was contained secondary metabolites which acts as a bioreductor, stabilizer and capping agent in the TiO2 NPs synthesis process. The Total Phenolic Content (TPC) and Total Flavonoid Content (TFC) of the ethanol extract of avocado fruit peel are 79,75 mg GAE/g and 21,74 mg QE/g. Chitosan/TiO2 nanocomposites were prepared in the form of beads with a ratio of chitosan to TiO2 (w/w) of 1:1. 1:2 and 2:1. Characterization of the resulting materials were carried out using X-ray Diffraction, Fourier transform Infrared spectroscopy, Scanning Electron Microscopy-Energy-Dispersive X-Ray Spectroscopy (SEM-EDX), Diffuse Reflectance Spectroscopy (UV-Vis DRS) and Brunauer Emmett Teller (BET) instruments. The synthesized TiO2 NPs have anatase and rutile phases with an average crystallite size is 19.28 nm and spherical shape particles. Chitosan/TiO2 nanocomposite beads with the ratio (w/w) 1:1, 1:2 and 2:1 have smaller average crystallite size than that of TiO2 NPs that is 14.49 nm; 11.21 nm; 9.41 nm, respectively. Chitosan/TiO2 1:1 nanocomposite bead has a smaller band gap energy (3.21 eV) than that of TiO2 NPs (3.26 eV). The results of the photocatalytic activity on rhodamine B (RhB) dye removal showed that the chitosan/TiO2 1:1 and had higher photocatalytic activity than that of chitosan/TiO2 1:1 and 2:1 nanocomposite beads. Chitosan/TiO2 1:1 nanocomposite bead was able to remove RhB dye up to 52.74% after being irradiated under ultra violet light and 94.98% after being irradiated under sunlight for 120 minutes on the optimum conditions of initial pH of RhB solution of 11, photocatalyst mass of 300 mg and initial RhB concentration of 1 ppm. Keywords: Biosynthesis, photocatalyst, beads, chitosan/TiO2, rhodamine B
GREEN SYNTHESIS NANOPARTIKEL TIO2 DAN MODIFIKASINYA DENGAN KITOSAN UNTUK PENGHILANGAN RHODAMIN B (Devi Andalusia, 2025)
SINTESIS KOMPOSIT BEADS TERNARY RNTIO2/ZNS/GRAFENA OKSIDA/KITOSAN DAN RNAPLIKASINYA PADA DEGRADASI RNFOTOKATALITIK TETRASIKLIN DIBAWAH RNCAHAYA TAMPAK (SHAFARANI, 2025)
DEGRADASI ZAT WARNA NAPHTHOL BLUE BLACK DAN RHODAMIN B MENGGUNAKAN FOTOKATALIS α-FE2O3-TIO2/KITOSAN TERIMOBILISASI PADA PLAT KACA (ALIFIA ZUKFIRA ARIANI, 2024)
PENGHILANGAN ZAT WARNA RHODAMIN B MENGGUNAKAN FOTOKATALIS KOMPOSIT CAO/TIO2 MENGGUNAKAN CANGKANG KERANG DARAH (ANADARA GRANOSA) SEBAGAI SUMBER CAO (FATIN NAFISA, 2023)
DEGRADASI ZAT WARNA RHODAMIN B MENGGUNAKAN FOTOKATALIS α-FE2O3-TIO2/KITOSAN-TERADSORPSI NAPHTHOL BLUE BLACK (NBB) YANG TERIMOBILISASI DENGAN SISTEM DUA LAPIS (FARLA NADHIRA PUTRI, 2025)