Electronic Theses and Dissertation

Penelitian ini bertujuan untuk mensintesis dan karakterisasi koloid logam Fe0 yang diimpregnasi pada serat nilon untuk mereduksi logam berat Cr(VI). Garam besi klorida dicampurkan dengan larutan polivinil alkohol (PVA) direduksi oleh ekstrak kulit jeruk bali membentuk koloid logam Fe0. Koloid logam Fe0 diimpregnasi pada serat nilon. Komposit tersebut kemudian diuji kemampuannya sebagai reduktor dengan mereduksi logam berat Cr(VI). Hasil uji XRD didapatkan puncak 2θ = 43,4° dan 65,02° yang menunjukkan keberadaan Fe0. Hasil uji FTIR didapatkan puncak pita serapan koloid Fe0 yang tidak jauh berbeda dari PVA dan ekstrak kulit jeruk bali, menunjukkan keberadaan gugus O-H, C-H, C=O, C-O dan C-N, membuktikan peran keduanya sebagai stabilizing dan capping agent dalam sintesis koloid Fe0. Uji SEM menunjukkan koloid Fe0 yang terimpregnasi pada serat nilon memiliki bentuk irregular, dan terselimuti PVA serta senyawa organik dibuktikan oleh hasil EDS berupa kandungan unsur Fe, C, dan O sebesar 17%, 56,9% dan 24,9% secara berturut-turut. Pemeriksaan dengan mikroskop optik menunjukkan ketebalan koloid Fe0 pada serat nilon sebesar 37,412 µm dan 82,43 mg/L Fe terkandung dalam tiap sampel komposi sesuai hasil uji AAS. Komposit berhasil mereduksi Cr(VI) menjadi Cr(III) ditunjukkan oleh penurunan konsentrasi Cr(VI) seiring berjalannya proses reduksi, dengan efisiensi reduksi tertinggi sebesar 67,47% pada waktu ke-120 menit, dimana reaksi mencapai kesetimbangan.

This study aims to synthesize and characterize Fe0 metal colloids impregnated onto nylon fibers for the reduction of the heavy metal Cr(VI). Iron chloride salt was mixed with a polyvinyl alcohol (PVA) solution and reduced by pomelo peel extract to form Fe0 metal colloids. The Fe0 metal colloids were impregnated onto nylon fibers. The composite was then tested for its reducing ability by reducing Cr(VI) heavy metal. XRD testing revealed peaks at 2θ = 43.4° and 65.02°, indicating the presence of Fe0. FTIR analysis showed absorption peaks of Fe0 colloid that were similar to those of PVA and pomelo peel extract, indicating the presence of O-H, C-H, C=O, C-O, and C-N groups, proving their roles as stabilizing and capping agents in the synthesis of Fe0 colloid. SEM analysis showed that the Fe0 colloids impregnated onto the nylon fibers had an irregular shape and were covered with PVA and organic compounds, as evidenced by EDS results with Fe, C, and O contents of 17%, 56.9%, and 24.9%, respectively. Optical microscopy revealed that the thickness of Fe0 colloid on the nylon fibers was 37.412 µm, and each composite sample contained 82.43 mg/L Fe, according to AAS results. The composite successfully reduced Cr(VI) to Cr(III), as indicated by the decrease in Cr(VI) concentration during the reduction process, with the highest reduction efficiency of 67.47% at 120 minutes, where the reaction reached equilibrium.