Sealer merupakan pasta pengisi yang penting digunakan dalam perawatan endodontik. Material sealer yang banyak digunakan sekarang adalah material berbasis bio-ceramic, seperti Mineral Trioxide Aggregate (MTA) karena memiliki sifat yang biokompatibel serta dapat memicu perbaikan saluran akar. Material MTA terbuat dari bahan dasar berupa batu gamping yang tersusun atas mineral CaCO3 (kalsium karbonat) yang tinggi. Penelitian ini bertujuan untuk mengetahui kadar unsur, fasa, ukuran, dan struktur kristal batu gamping Aceh sebagai bahan baku sealer endodontik. Sampel batu gamping Aceh yang diambil dari kecamatan Lhoknga dan Muara Tiga kemudian dikalsinasi pada suhu 900°C dengan tanur selama 1 jam dan dikarakterisasi dengan X-Ray Fluorescence (XRF) dan X-Ray Diffraction (XRD). Hasil analisis karakterisasi dengan XRF menunjukkan bahwa kadar kalsium dalam batu gamping Lhoknga (sebelum kalsinasi 99,48% dan setelah kalsinasi 99,54%) dan Muara Tiga (sebelum kalsinasi 99,32% dan setelah kalsinasi 99,75%) tinggi dengan kadar pengotor yang sangat sedikit. Senyawa mineral yang teridentifikasi dengan XRD sebelum kalsinasi pada kedua batu gamping adalah fasa kalsit dan periklase. Setelah kalsinasi, Hasil XRD menunjukkan bahwa fasa batu gamping Lhoknga adalah kalsit dan kalsium hidroksida sedangkan batu gamping Muara Tiga adalah kalsit dan kalsium oksida. Keduanya memiliki fasa utama berupa kalsit dengan bentuk kristal trigonal. Disimpulkan bahwa batu gamping Aceh dapat digunakan sebagai bahan baku sealer endodontik karena memiliki kadar kalsium yang tinggi.

Kata kunci: Batu gamping, Aceh, Sealer endodontik, XRF, XRD

Sealers are important filling pastes used in endodontic treatment. Sealer materials that are widely used today are bioceramic-based materials, such as Mineral Trioxide Aggregate (MTA) because of its biocompatible properties and can induce root canal repair. MTA is made from limestone which is composed of high calcium carbonate (CaCO3) mineral. The objective of this study was to determine the elemental content, phase, crystal size and structure of Aceh limestone as a raw material for endodontic sealers. Aceh limestone samples were collected from Lhoknga and Muara Tiga and subjected to calcination at 900°C for one hour in a furnace. The samples were then analyzed using X-ray fluorescence (XRF) and X-ray diffraction (XRD). The XRF analysis revealed that the limestone from both locations had high calcium content (99.48% and 99.32% before calcination, and 99.54% and 99.75% after calcination, respectively), with minimal impurities. The XRD analysis identified calcite and periclase phases in both limestones before calcination. After calcination, the mineral compounds identified through XRD analysis of Lhoknga limestone are calcite and calcium hydroxide, whereas in Muara Tiga limestone are calcite and calcium oxide. Both contained calcite as the main phase with a trigonal crystal shape. Aceh limestone is an excellent raw material for endodontic sealers due to its high calcium content. Keywords: Limestone, Aceh, Endodontic sealer, XRF, XRD.