Telah dilakukan fabrikasi DSSC menggunakan Mg doped TiO2 sebagai fotoelektroda
dan campuran klorofil-antosianin sebagai dye. Penelitian ini bertujuan untuk
mempelajari pengaruh variasi konsentrasi masing-masing sumber dye dalam dye
campuran. Campuran dye divariasikan konsentrasi campurannya sebesar 1:1, 1:2,
1:3, 2:1, dan 3:1 klorofil-antosianin. Pasta Mg doped TiO2 dideposisikan di atas
substrat dengan metode Doctor Blade. Lapisan Mg doped TiO2 dikarakterisasi
mengunakan XRD, SEM dan Spektrofotometer UV-Vis. Fasa yang muncul dari hasil
karakterisasi adalah TiO2 dan MgO. Ketidak munculan fasa lain diperkuat dengan
pengujian SEM dan analisis EDS yang membuktikan tidak terdapat impuritas. Energi
gap dari lapisan Mg doped TiO2 hasil karakterisasi adalah 3,03 eV. Campuran dye
dikarakterisasi menggunakan Spektrofotometer UV-Vis dan FTIR. Klorofil dan
antosianin berhasil diekstrak dari sumber. Energi gap dye campuran semakin besar
seiring meningkatnya konsentrasi antosianin. Hasil karakterisasi DSSC menunjukkan
efisiensi semakin besar pada penambahan konsentrasi klorofil yang lebih banyak.

DSSC fabrication using Mg doped TiO2 as photoelectrode and chlorophyll anthocyanin mixture as dye has been conducted. This research aims to study the effect of variations in the concentration of each dye source in a mixed dye. The dye mixture was varied in concentration by 1:1, 1:2, 1:3, 2:1, and 3:1 chlorophyllanthocyanin. Mg doped TiO2 paste was deposited on the substrate by Doctor Blade method. Mg doped TiO2 layers were characterized using XRD, SEM and UV-Vis spectrophotometer. The phases that appear from the characterization results are TiO2 and MgO, the absence of other phases is reinforced by SEM testing and EDS analysis which proves there are no impurities. Energy gap of Mg doped TiO2 layer of characterization results is 3.03 eV. The dye mixture was characterized using UV-Vis Spectrophotometer and FTIR. Chlorophyll and anthocyanin were successfully extracted from the source. The gap energy of the mixed dye is getting bigger as the anthocyanin concentration increases. The DSSC characterization results showed that the efficiency increased with the addition of more chlorophyll concentration.