PEMBUATAN KOMPOSIT KITOSAN-ASPARAGIN MAGNETIK BERIKAT SILANG PEDGE DAN APLIKASINYA SEBAGAI ADSORBEN METHYLENE BLUE
Pengarang
MUTAWALLY - Personal Name;
Dosen Pembimbing
Rahmi - 197209271999032001 - Dosen Pembimbing I
Nomor Pokok Mahasiswa
1508103010058
Fakultas & Prodi
Fakultas MIPA / Kimia (S1) / PDDIKTI : 47201
Subject
Kata Kunci
Penerbit
Banda Aceh : Fakultas MIPA Kimia., 2023
Bahasa
No Classification
-
Literature Searching Service
Hard copy atau foto copy dari buku ini dapat diberikan dengan syarat ketentuan berlaku, jika berminat, silahkan hubungi via telegram (Chat Services LSS)
Modifikasi kitosan magnetik berikat silang PEDGE dengan asparagin untuk menyerap metilen biru telah dilakukan. Modifikasi dilakukan dengan variasi komposisi asparagin dimana komposisi kitosan, PEDGE dan pasir besi dibuat tetap. Komposit terbaik di uji daya serapnya terhadap larutan metilen biru dengan memvariasikan waktu, pH dan konsentrasi larutan metilen biru. Berdasarkan hasil penelitian, kondisi adsorpsi optimum diperoleh pada pH 10 dengan waktu kontak 30 menit. Isoterm adsorpsi kitosan-asparagin magnetik berikat silang PEDGE mengikuti isoterm Langmuir dan Freundlich dengan kapasitas serapan 37,453mg/g. Karakterisasi FTIR mengkonfirmasi terbantuknya komposit kitosan-asparagin magnetik berikat silang PEDGE. Hasil SEM menunjukkan permukaan adsorben pada kitosan halus sedangkan kitosan-asparagin magnetik berikat silang PEDGE menunjukkan permukaan adsorben lebih kasar. Hasil XRD mennujukkan terjadinya penurunan kristalinitas kitosan setelah dimodifikasi
Modification of magnetic PEDGE crosslinked chitosan with asparagine to adsorb methylene blue has been conducted. The modification was performed out by varying the composition of asparagine where the composition of chitosan, PEDGE and iron sand was made fixed. The best composite was tested for its adsorption capacity of methylene blue solution by varying the time, pH and concentration of methylene blue solution. Based on results, the optimum adsorption conditions were obtained at pH 10 with a contact time of 30 minutes. The magnetic PEDGE crosslinked chitosan-asparagine adsorption isotherm follows the Langmuir and Freundlich isotherm with an adsorption capacity of 37,453 mg/g. FT-IR characterization confirmed the formation of a magnetic PEDGE crosslinked chitosan-asparagine composite. The SEM results showed that the surface of the adsorbent on chitosan was smooth, while the magnetic chitosan-asparagine crosslinked PEDGE showed a rougher adsorbent surface. The XRD results showed a decrease in chitosan crystallinity after modification.
PEMBUATAN KOMPOSIT KITOSAN MAGNETIK TERSULFONASI BERIKATAN SILANG POLIETILEN GLIKOL DIGLISIDIL ETER (PEDGE) SEBAGAI ADSORBEN METILEN BIRU (Haya Fathana, 2018)
PEMBUATAN DAN KARAKTERISASI KOMPOSIT KITOSAN MAGNETIK BERIKATAN SILANG H2SO4 DAN APLIKASINYA SEBAGAI ADSORBEN METHYLENE BLUE (ISHMATURRAHMI, 2018)
PEMBUATAN KOMPOSIT KITOSAN BERIKATAN SILANG POLIETILEN GLIKOL DIGLISIDIL ETER (PEDGE)/ARANG AKTIF UNTUK PENYERAPAN ION LOGAM KADMIUM (RIZKI NURFATIMAH, 2017)
MODIFIKASI KITOSAN MENGGUNAKAN PASIR BESI, PENGIKAT SILANG PEGDE DAN HIDROLISAT PROTEIN DARI BIJI PETAI CINA SEBAGAI ADSORBEN ION LOGAM KADMIUM (CUT PUTRI AULIA, 2020)
MODIFIKASI KITOSAN MENGGUNAKAN PASIR BESI, PENGIKAT SILANG PEGDE DAN ASAM GLUTAMAT SEBAGAI ADSORBEN ION LOGAM KADMIUM (SHABRINA, 2021)