Sintesis fotokatalis komposit CaO/TiO2 menggunakan metode impregnasi basah dan
uji aktivitas fotokatalitiknya pada degradasi zat warna rhodamin B telah dilakukan.
Kalsium oksida dipreparasi dari cangkang kerang darah melalui metode dekomposisi
termal. Titanium dioksida disintesis menggunakan (Ti[OCH(CH3)2]4) sebagai
prekursor dengan metode sol-gel. Karakterisasi material yang dihasilkan dilakukan
menggunakan instrumen X-Ray Diffraction (XRD), Scanning Electron MicroscopyEnergy-Dispersive X-Ray Spectroscopy (SEM-EDS), Brunaeur Emmet Teller (BET)
dan Diffuse Reflectance Spectroscopy UV-Vis (DRS UV-Vis). TiO2 yang diperoleh
memiliki fasa anatase dan CaO memiliki fasa portlandit. Komposit 15%-CaO/TiO2
memiliki luas permukaan yang lebih rendah dari TiO2, energi celah pita sedikit lebih
besar dari TiO2 dan ukuran rata-rata pori lebih besar dari TiO2. Hasil uji aktivitas
fotokatalitik pada penghilangan zat warna rhodamin B (RhB) menunjukkan komposit
15%-CaO/TiO2 memiliki aktivitas yang paling tinggi dibandingkan dengan
penambahan CaO 5% b/b, 25%b/b dan 35% b/b. Komposit 15%-CaO/TiO2 dapat
mendegradasi zat warna rhodamin B hingga 97,77% dibawah irradiasi sinar UV pada
kondisi optimum pH larutan rhodamin B 5, massa fotokatalis 250 mg, konsentrasi zat
warna rhodamin B 5 ppm dan waktu irradiasi selama 120 menit. Komposit 15%-
CaO/TiO2 memiliki aktivitas lebih tinggi dibawah irradiasi sinar matahari
dibandingkan dengan sinar UV. Penambahan CaO terbukti dapat meningkatkan
aktivitas fotokatalitik TiO2.

Synthesis of CaO/TiO2 composite photocatalysts using the wet impregnation method and the evaluation of their photocatalytic activity on the degradation of rhodamine B dye has been carried out. Calcium oxide was prepared from blood clam shells through the thermal decomposition method. Titanium dioxide was synthesized using (Ti[OCH(CH3)2]4) as a precursor by the sol-gel method. The resulting materials characterization were carried out using X-Ray Diffraction (XRD) instruments, Scanning Electron Microscopy-Energy-Dispersive X-Ray Spectroscopy (SEM-EDS), Brunaeur Emmet Teller (BET), and Diffuse Reflectance Spectroscopy UV-Vis (DRS UV-Vis). TiO2 obtained has an anatase phase and CaO has a portlandite phase. The specific surface area of the 15%-CaO/TiO2 composite was lower than that of TiO2, while it is band gap energy was slightly higher than that of TiO2 and the average pore size was bigger than TiO2. The results of the photocatalytic activity evaluation on the removal of rhodamine B (RhB) dye showed that the 15%-CaO/TiO2 composite has the highest activity compared to the addition of CaO 5% w/w, 25% w/w and 35% w/w. The 15%-CaO/TiO2 composite can degrade rhodamine B dye up to 97.77% under UV light irradiation at optimum conditions the initial pH of RhB solution 5, photocatalyst mass of 250 mg, the concentration of rhodamine B dye of 5 ppm and irradiation time of 120 minutes. Composite 15%-CaO/TiO2 has higher activity under sunlight irradiation than that of UV light irradiation. The addition of CaO can increase the photocatalytic activity of TiO2.