PENGARUH KANDUNGAN TULANGAN SATU ARAH TERHADAP KUAT TEKAN BETON MUTU TINGGI DENGAN BENDA UJI SILINDER DIAMETER 10X10 CM
Pengarang
SAMSUIR - Personal Name;
Dosen Pembimbing
M. Arief Rahman Panjaitan - 198511112012121003 - Dosen Pembimbing I
Nomor Pokok Mahasiswa
1704001010044
Fakultas & Prodi
Fakultas Teknik / Teknik Sipil (D3) / PDDIKTI : 22401
Penerbit
Banda Aceh : Fak. Teknik Sipil Diploma III., 2022
Bahasa
Indonesia
No Classification
624.183 4
Literature Searching Service
Hard copy atau foto copy dari buku ini dapat diberikan dengan syarat ketentuan berlaku, jika berminat, silahkan hubungi via telegram (Chat Services LSS)
Beton mutu tinggi adalah beton yang memiliki kuat tekan lebih tinggi dibandingkan beton normal biasa. Menurut PD T-04-2004-C tentang tata cara pembuatan dan pelaksanaan beton berkekuatan tinggi, yang tergolong beton bermutu tinggi adalah beton yang memiliki kuat tekan antara 40-80 MPa. Penelitian ini bertujuan untuk mengetahui seberapa berpengaruh Tulangan satu arah terhadap kuat tekan beton, dengan menggunakan silinder sebanyak 15 buah dengar ukuran 10 cm × 10 cm. Hasil dari penelitian ini menghasilkan kuat tekan rata-rata untuk beton yang menggunakan tulangan posisi 1/2 dari tinggi benda uji bernilai 62,97 N/mm² , Setelah dikalikan dengan faktor koreksi menghasilkan nilai rata-rata 66,34 N/mm², sedangkan untuk nilai rata-rata pada benda uji yang menggunakan tulangan posisi 1/4 dari tinggi benda uji bernilai 56,79 N/mm²,setelah dikalikan dengan faktor koreksi menghasilkan kuat tekan rata-rata bernilai 59,96 N/mm²,dan untuk benda uji tanpa menggunakan tulangan menghasilkan nilai rata-rata 72,32 N/mm².
Kata kunci: Beton mutu tinggi, kandungan tulangan satu arah, kuat tekan beton. L/D = 1
High strength concrete is concrete that has a higher compressive strength than ordinary normal concrete. According to PD T-04-2004-C concerning procedures for the manufacture and implementation of high-strength concrete, high-quality concrete is classified as concrete with a compressive strength of between 40-80 MPa. This study aims to determine how influential one-way reinforcement is on the compressive strength of concrete, using 15 cylinders with a size of 10 cm × 10 cm. The results of this study produce an average compressive strength for concrete that uses reinforcement position 1/2 of the height of the test object is worth 62.97 N/mm², after being multiplied by a correction factor produces an average value of 66.34 N/mm², while for the average value of the test object using the reinforcement position 1/4 of the height of the test object is 56.79 N/mm², after multiplied by the correction factor produces an average compressive strength of 59.96 N/mm², and for the specimen without using reinforcement produces an average value of 72.32 N/mm². Keywords: High strength concrete, one-way reinforcement content, compressive strength of concrete. L/D = 1
PENGARUH KANDUNGAN TULANGAN SATU ARAH TERHADAP KUAT TEKAN BETON MUTU TINGGI DENGAN BENDA UJI SILINDER DIAMETER 10X10 CM (SAMSUIR, 2022)
PENGARUH KANDUNGAN TULANGAN DUA ARAH TERHADAP KUAT TEKAN BETON MUTU TINGGI DENGAN BENDA UJI SILINDER DIAMETER 10X10CM (MULISSARUDIN, 2022)
PENGARUH KANDUNGAN TULANGAN DUA ARAH TERHADAP KUAT TEKAN BETON MUTU TINGGI (HERU MITRA WAHYUDI, 2022)
STUDI PERILAKU KUAT LEKAT (BOND STRENGTH) ANTARA BESI TULANGAN DENGAN BETON BUSA (FOAMED CONCRETE) DAN BETON NORMAL (NORMAL CONCRETE) (Joko Purnomo, 2024)
PENGARUH PENGGUNAAN POLYPROPYLENE FIBER PADA KUAT TEKAN BETON MUTU TINGGI PASCA BAKAR `RN(SUNTU PENELITIAN PEMHAKARAN BETON PADA SUHU 400°C SELAMA 5 JAM) (Safriana, 2024)