Electronic Theses and Dissertation

Keramik berpori berbasis lempung berpotensi digunakan sebagai media filtrasi air karena memiliki struktur pori yang mampu menyaring kontaminan. salah satu faktor yang memengaruhi sifat fisis dan kualitas filtrasi keramik berpori adalah ukuran partikel arang sekam padi sebagai agen pembentuk pori. penelitian ini bertujuan untuk mengetahui pengaruh variasi ukuran partikel arang sekam padi terhadap sifat fisis dan kualitas filtrasi keramik berpori, serta menentukan ukuran partikel optimum yang memberikan keseimbangan antara porositas dan kualitas filtrasi. keramik berpori dibuat menggunakan variasi ukuran partikel arang sekam padi 40, 60, 80, 100, dan 120 mesh, kemudian disintering dengan laju pemanasan 5 °c/menit, ditahan pada suhu 450 °c selama 2 jam, dan dilanjutkan pada suhu 900 °c selama 4 jam. karakterisasi sifat fisis meliputi bulk density, porositas, laju aliran, dan permeabilitas, sedangkan kualitas filtrasi dianalisis berdasarkan parameter total dissolved solids (tds), konduktivitas listrik, dan kekeruhan. hasil penelitian menunjukkan bahwa semakin halus ukuran partikel arang sekam padi, bulk density meningkat dari 0,88 g/cm³ menjadi 1,06 g/cm³, sedangkan porositas menurun dari 53,9% menjadi 46,6%. ukuran partikel 120 mesh memberikan kualitas filtrasi terbaik dengan efisiensi penyisihan tds sebesar 76,92% pada air gambut, 43,18% pada air sumur, dan 24,66% pada air limbah penyulingan emas. konduktivitas listrik juga menurun dari 535 μs/cm menjadi 116,5 μs/cm pada air gambut, dari 527 μs/cm menjadi 300 μs/cm pada air sumur, dan dari 876 μs/cm menjadi 658 μs/cm pada air limbah penyulingan emas, sedangkan nilai kekeruhan seluruh sampel hasil filtrasi mencapai 0 ntu. berdasarkan hasil tersebut, ukuran partikel arang sekam padi 120 mesh merupakan kondisi optimum untuk menghasilkan keseimbangan antara sifat fisis dan kualitas filtrasi. kata kunci: keramik berpori, arang sekam padi, ukuran partikel, porositas, kualitas filtrasi.

Clay-based porous ceramics have great potential as water filtration media due to their porous structure, which enables the removal of contaminants from water. One of the factors influencing the physical properties and filtration performance of porous ceramics is the particle size of rice husk charcoal used as a pore-forming agent. This study aimed to investigate the effect of rice husk charcoal particle size on the physical properties and filtration performance of clay-based porous ceramics, as well as to determine the optimum particle size that provides a balance between porosity and filtration performance. The porous ceramics were fabricated using rice husk charcoal with particle sizes of 40, 60, 80, 100, and 120 mesh. The samples were sintered at a heating rate of 5 °C/min, held at 450 °C for 2 h, and then at 900 °C for 4 h. The physical properties were characterized in terms of bulk density, porosity, flow rate, and permeability, while the filtration performance was evaluated based on total dissolved solids (TDS), electrical conductivity, and turbidity. The results showed that decreasing the particle size of rice husk charcoal increased the bulk density from 0.88 g/cm³ to 1.06 g/cm³, whereas the porosity decreased from 53.9% to 46.6%. The 120-mesh particle size exhibited the best filtration performance, achieving TDS removal efficiencies of 76.92% for peat water, 43.18% for well water, and 24.66% for gold-refining wastewater. In addition, the electrical conductivity decreased from 535 μS/cm to 116.5 μS/cm for peat water, from 527 μS/cm to 300 μS/cm for well water, and from 876 μS/cm to 658 μS/cm for gold-refining wastewater, while the turbidity of all filtered water samples reached 0 NTU. These findings indicate that the 120-mesh rice husk charcoal particle size is the optimum condition for achieving a balance between the physical properties and filtration performance of clay-based porous ceramics. Keywords: clay-based porous ceramics, rice husk charcoal, particle size, porosity, filtration performance.