Resin akrilik polimetil metakrilat (pmma) merupakan bahan basis gigi tiruan yang banyak digunakan karena sifat estetik, biokompatibilitas, dan kemudahan manipulasi, tetapi memiliki kelemahan berupa impact strength yang rendah. penelitian ini bertujuan untuk mengetahui pengaruh penambahan nanopartikel zirkonia (zro2) terhadap nilai impact strength resin akrilik self-cured pasca reparasi. penelitian eksperimental laboratorik ini menggunakan empat kelompok, yaitu kelompok kontrol tanpa zro2 serta kelompok perlakuan dengan konsentrasi 0,5%, 0,75%, dan 1% zro2. pengujian dilakukan menggunakan metode charpy tanpa takik sesuai standar astm d5942-96. hasil penelitian menunjukkan peningkatan impact strength pada konsentrasi 0,5% dan mencapai nilai tertinggi pada 0,75%, sedangkan konsentrasi 1% mengalami penurunan. peningkatan pada 0,75% dipengaruhi oleh dispersi partikel yang homogen dan ikatan matriks-partikel yang baik, sementara penurunan pada 1% disebabkan oleh aglomerasi partikel yang menjadi pusat konsentrasi tegangan. penelitian ini menyimpulkan bahwa penambahan nanopartikel zro2 dengan konsentrasi 0,75% merupakan konsentrasi optimum untuk meningkatkan impact strength resin akrilik self-cured pasca reparasi. kata kunci: impact strength, resin akrilik, nanopartikel zirkonia, reparasi gigi tiruan

Polymethyl methacrylate (PMMA) is widely used as a denture base material due to its esthetics, biocompatibility, and ease of manipulation; however, it has a major drawback of low impact strength. This study aimed to evaluate the effect of zirconia nanoparticle (ZrO2) addition on the impact strength of repaired self-cured acrylic denture base resin. This laboratory experimental study consisted of four groups: a control group without ZrO2 and treatment groups containing 0.5%, 0.75%, and 1% ZrO2. Impact strength testing was performed using the Charpy method without a notch following ASTM D5942-96 standards. The results demonstrated an increase in impact strength at 0.5% and the highest value at 0.75%, followed by a decrease at 1%. The increase at 0.75% was attributed to homogeneous nanoparticle dispersion and improved particle-matrix bonding, whereas the decrease at 1% resulted from particle agglomeration, which acted as stress concentration sites. It is concluded that the addition of 0.75% ZrO2 nanoparticles is the optimum concentration for enhancing the impact strength of repaired self-cured acrylic denture base resin. Keywords: Impact strength, acrylic resin, zirconia nanoparticles, denture repair