Polymethyl methacrylate (pmma) banyak digunakan sebagai bahan basis gigi tiruan karena memiliki sifat estetik yang baik, biokompatibel, serta mudah dimanipulasi. kekurangan utama bahan ini kekerasan yang relatif rendah, terutama setelah proses reparasi. penelitian ini bertujuan untuk mengetahui pengaruh penambahan nanopartikel zirkonia (nano-zro₂) terhadap kekerasan basis gigi tiruan resin akrilik self-cured setelah reparasi. penelitian eksperimental laboratorium ini terdiri atas empat kelompok, yaitu kelompok kontrol tanpa penambahan zro₂, serta kelompok dengan penambahan nano-zro₂ sebesar 1%, 3%, dan 5%. pengujian kekerasan dilakukan menggunakan uji vickers, dan data dianalisis secara statistik. hasil penelitian menunjukkan bahwa nilai kekerasan tertinggi terdapat pada kelompok 5% zro₂ dengan rata-rata 15,87 hv, sedangkan nilai terendah terdapat pada kelompok 3% zro₂ dengan rata-rata 14,01 hv. kelompok 1% zro₂ memiliki nilai kekerasan 14,05 hv, sedikit lebih tinggi dibanding kelompok 3%, sementara kelompok kontrol memiliki nilai 14,52 hv. data terdistribusi normal dan homogen. analisis menggunakan uji one-way anova menunjukkan perbedaan yang signifikan antar kelompok (p < 0,05). uji post hoc menunjukkan bahwa kelompok 5% memiliki nilai kekerasan yang secara signifikan lebih tinggi dibanding kelompok lainnya. kesimpulan dari penelitian ini adalah konsentrasi optimal nanopartikel zro₂ sebagai filler untuk meningkatkan kekerasan basis gigi tiruan resin akrilik self-cured pasca reparasi adalah 5%.

Polymethyl methacrylate (PMMA) is widely used as a denture base material due to its good esthetic properties, biocompatibility, and ease of manipulation. However, its main limitation is its relatively low hardness, especially after the repair process. This study aimed to determine the effect of adding zirconia nanoparticles (nano- ZrO₂) on the hardness of repaired acrylic denture base. This laboratory experimental study consisted of four groups: a control group without ZrO₂ and three treatment groups with the addition of 1%, 3%, and 5% nano-ZrO₂. Hardness testing was performed using the Vickers hardness test, and the data were statistically analyzed. The results showed that the highest hardness value was found in the 5% ZrO₂ group with a mean of 15.87 HV, while the lowest was observed in the 3% ZrO₂ group with a mean of 14.01 HV. The 1% ZrO₂ group showed a hardness value of 14.05 HV, slightly higher than the 3% group, while the control group had a value of 14.52 HV. The data were normally distributed and homogeneous. One-way ANOVA revealed a significant difference among the groups (p < 0.05). Post Hoc analysis indicated that the 5% group had a significantly higher hardness value than all other groups. The conclusion of this study is that the optimal concentration of ZrO₂ nanoparticles as a filler to enhance the hardness of self-cured acrylic resin denture base after repair is 5%