Electronic Theses and Dissertation

Arisa munira. 2025. pencemaran air akibat logam berat seperti nikel (ni²⁺) menjadi isu serius karena bersifat toksik dan sulit terurai di lingkungan. penelitian ini bertujuan untuk membuat komposit kitosan yang diimobilisasi pada pelet serbuk gergaji sebagai adsorben untuk mengurangi ion nikel terlarut dalam air. komposit dibuat dengan mencampur serbuk gergaji dan tepung tapioka, dicetak menjadi pelet, kemudian disalut menggunakan larutan kitosan. karakterisasi dilakukan dengan sem dan ftir. uji adsorpsi dilakukan dengan variasi massa adsorben dan waktu kontak menggunakan larutan ni(no₃)₂•6h₂o. konsentrasi nikel sebelum dan sesudah adsorpsi dianalisis menggunakan spektrofotometer uv-vis. hasil penelitian menunjukkan pelet serbuk gergaji dan pelet salut kitosan dapat menyerap ion nikel pada waktu optimum 10 menit berturut-turut sebanyak 730,003 dan 750,00 mg/l dengan efisiensi berturut-turut 33,26% dan 34,17%. %. kapasitas adsorpsi yang diperoleh pada pelet serbuk gergaji dan pelet salut kitosan sebesar 400 butir dengan berat adsorben berturut-turut 8,165 dan 7,308 gram. tipe isoterm dari penelitian ini pada pelet serbuk gergaji dan pelet serbuk gergaji salut kitosan mengikut isoterm freundlich dengan persamaan pelet serbuk gergaji y= 29,407x – 94,13 dengan nilai r2 sebesar 0,9588 dan persamaan pelet serbuk gergaji salut kitosan yaitu y = 1,167x- 2,6682 dengan nilai r2 sebesar 0,9994. komposit kitosan juga menunjukkan ketahanan fisik yang baik terhadap suhu tinggi. uji kolom menunjukkan konsentrasi ion nikel yang teradsorpsi pada pelet serbuk gergaji dan pelet salut kitosan berturut-turut sebesar 500,00 dan 773.74 mg/l dengan efesiensi penyerapan 23,21% dan 35,89%. hasil regenerasi adsorben menunjukkan konsentrasi pada pelet serbuk gergaji dan pelet salut kitosan berturut-turut sebesar 66,67 dan 103,33 mg/l dengan efisiensi penyerapan 3,03% dan 10%. kata kunci: komposit kitosan, pelet serbuk gergaji, adsorpsi ion nikel, spektrofotometer uv-vis, sem, aas dan ftir

Arisa Munira. 2025. Water pollution due to heavy metals such as nickel (Ni²⁺) is a serious issue because it is toxic and difficult to decompose in the environment. This study aims to make a chitosan composite immobilized on sawdust pellets as an adsorbent to reduce dissolved nickel ions in water. The composite was made by mixing sawdust and tapioca flour, molded into pellets, then coated using a chitosan solution. Characterization was carried out using SEM and FTIR. Adsorption tests were carried out with variations in adsorbent mass and contact time using a Ni(NO₃)₂•6H₂O solution. The nickel concentration before and after adsorption was analyzed using a UV-Vis spectrophotometer. The results of the study showed that sawdust pellets and chitosan coated pellets could absorb nickel ions at an optimum time of 10 minutes, respectively, as much as 730.003 and 750.00 mg/L with efficiencies of 33.26% and 34.17%, respectively. The adsorption capacity obtained in sawdust pellets and chitosan coated pellets was 400 grains with adsorbent weights of 8.165 and 7.308 grams, respectively. The isotherm type of this study on sawdust pellets and chitosan coated sawdust pellets followed the Freundlich isotherm with the sawdust pellet equation y = 29.407x - 94.13 with an R2 value of 0.9588 and the chitosan coated sawdust pellet equation, namely y = 1.167x - 2.6682 with an R2 value of 0.9994. Chitosan composites also showed good physical resistance to high temperatures. Column tests showed that the concentrations of nickel ions adsorbed on sawdust pellets and chitosan-coated pellets were 500.00 and 773.74 mg/L, respectively, with adsorption efficiencies of 23.21% and 35.89%. Adsorbent regeneration results showed concentrations on sawdust pellets and chitosan-coated pellets of 66.67 and 103.33 mg/L, respectively, with adsorption efficiencies of 3.03% and 10%. Keywords: Chitosan composite, Sawdust pellets, Nickel ion adsorption UV-Vis spectrophotometer, SEM, AAS, and FTIR