Penelitian ini bertujuan untuk mensintesis, mengkarakterisasi, dan mengimmobilisasi kobalt nanopartikel pada serat nilon menggunakan ekstrak kulit jeruk bali. sintesis conps menggunakan metode greensynthesis melalui penggunaan ekstrak kulit jeruk bali sebagai reduktor agar lebih ramah lingkungan dan terjangkau. hasil sintesis conps ini dapat dimanfaatkan diberbagai bidang, salah satunya sebagai katalis. kobalt (ii) klorida heksahidrat dicampurkan dengan larutan pva direduksi oleh ekstrak kulit jeruk bali membentuk koloid co0 dan didiamkan selama kurang lebih 14 hari hingga membentuk film conps. film conps dikarakterisasi dengan uji xrd dan diperoleh sudut difraksi 2θ = 79,4° yang menunjukkan ukuran conps sebesar 58,65 nm. hasil ftir conps menunjukkan ada streaching vibration pada o-h, c-h, c=c, dan c=o. kandungan co0 berdasarkan hasil uji xrf menunjukkan sebesar 61,9 mass% dan kandungan oksida co2o3 64,4 mass%. koloid co0 diimmobilisasi pada serat nilon dengan pva sebagai perekat. koloid co0 yang telah terimmobilisasi dikarakterisasi dengan aas dan diperoleh hasil sebesar 62,014 mg/l. sn-pva-conps kemudian diuji kemampuannya sebagai reduktor dengan mereduksi cr(vi) 100 ppm. hasilnya diperoleh konsentrasi cr(vi) setelah direduksi sebesar 28,92 ppm pada menit ke-55. hasil ini menunjukkan bahwasanya sn-pva-conps cukup baik dalam mereduksi cr(vi). kata kunci: conps, serat nilon, ekstrak kulit jeruk bali, pva

This study aims to synthesize, characterize, and immobilize cobalt nanoparticles (CoNPs) on nylon fibers using pomelo (Citrus maxima) peel extract. The synthesis of CoNPs was carried out using a green synthesis method, utilizing pomelo peel extract as a reducing agent to make the process more environmentally friendly and cost-effective. The synthesized CoNPs can be applied in various fields, one of which is as a catalyst. Cobalt(II) chloride hexahydrate was mixed with a PVA solution and reduced by pomelo peel extract to form a Co⁰ colloid, which was then left to stand for approximately 14 days to form a CoNPs film. The CoNPs film was characterized using XRD, and a diffraction peak at 2θ = 79.4° was observed, indicating a particle size of 58.65 nm. FTIR analysis of the CoNPs showed stretching vibrations corresponding to O–H, C–H, C=C, and C=O functional groups. The Co⁰ content based on XRF analysis was found to be 61.9 mass%, while the Co₂O₃ oxide content was 64.4 mass%. The Co⁰ colloid was immobilized onto nylon fibers using PVA as an adhesive. The immobilized Co⁰ was then characterized using AAS, with the result showing a cobalt concentration of 62.014 mg/L. The SN-PVA-CoNPs were further tested for their reducing ability by applying them to reduce 100 ppm Cr(VI). The result showed that the Cr(VI) concentration decreased to 28.92 ppm after 55 minutes. These findings indicate that SN-PVA-CoNPs exhibit promising potential in reducing Cr(VI). Keywords: CoNPs, Nylon Fibers, Pomelo Peel Extract, PVA