Penelitian ini dilakukan untuk mempelajari pengaruh panjang serat sabut kelapa terhadap kekuatan tarik komposit epoxi yang di buat dengan proses hand lay up. komposit serat sabut kelapa di buat dengan cetakan kaca ukuran 200 x 200 x 5 mm sebanyak 4 papan komposit dengan pengujian sebanyak 5 spesimen tiap variasi panjang serat sabut kelapa 2 mm, 4 mm, 6 mm, 200 mm. pengujian tarik dilakukan menggunakan mesin mts landmark servohydroulic test system dengan spesimen merujuk pada american standart testing and material d-638. hasil pengamatan struktur mikro bentuk patahan komposit variasi ukuran serat 2 mm, 4 mm dan 6 mm memiliki bentuk patahan ulet sedangkan bentuk patahan komposit variasi ukuran serat 200 mm yaitu retak yang menjalar pada daerah pemberian beban tarik dan belum mampu menerima gaya yang diberikan. dari hasil pengujian tarik didapatkan nilai rata-rata kekuatan tarik tertinggi pada komposit variari ukuran serat 6 mm sebesar 28,47 mpa dan nilai rata-rata kekuatan tarik terendah didapatkan pada komposit variasi ukuran serat 2 mm sebesar 7,94 mpa. nilai rata-rata kekuatan tarik pada spesimen 2mm, 4 mm, 6 mm dan 200 mm masing-masing memiliki nilai kekuatan tarik 7,94 mpa, 27,54 mpa, 28,47 mpa, 27,40 mpa.

This research was conducted to study the effect of coir fiber length coconut to the tensile strength of epoxy composites made by hand process lay ups. Coconut coir fiber composite made with 200 x glass mold 200 x 5 mm as many as 4 composite boards with a test of 5 specimens each variation in length of coco fiber 2 mm, 4 mm, 6 mm, 200 mm. Test The tensile strength is carried out using the MTS Landmark Servohydroulic Test System machine with specimens referring to American Standard Testing and Materials D-638. The results of observations of the microstructure of the composite fracture form with variations in fiber size 2 mm, 4 mm and 6 mm have a ductile fracture shape while the fracture form composite fiber size variation of 200 mm, namely cracks that spread in the tensile load and has not been able to accept the applied force. From the tensile test results obtained the highest average tensile strength value at composite of 6 mm fiber size variation of 28.47 MPa and the average value of The lowest tensile strength was found in the composite fiber size variation of 2 mm of 7.94 MPa. The average value of tensile strength on specimens 2mm, 4mm, 6 mm and 200 mm each have a tensile strength value of 7.94 MPa, 27.54 MPa, 28.47 MPa, 27.40 MPa.