IMMOBILISASI α-FE2O3/BENTONIT SEBAGAI FOTOKATALIS PADA FOTODEGRADASI ZAT WARNA METHYLENE BLUE
Pengarang
Shofi Nurul Sakinah - Personal Name;
Dosen Pembimbing
Sheilatina - 197808052003122001 - Dosen Pembimbing I
Julinawati - 197107011997022001 - Dosen Pembimbing II
Nomor Pokok Mahasiswa
1908103010015
Fakultas & Prodi
Fakultas MIPA / Kimia (S1) / PDDIKTI : 47201
Subject
Kata Kunci
Penerbit
Banda Aceh : Fakultas MIPA Kimia., 2024
Bahasa
No Classification
-
Literature Searching Service
Hard copy atau foto copy dari buku ini dapat diberikan dengan syarat ketentuan berlaku, jika berminat, silahkan hubungi via telegram (Chat Services LSS)
Immobilisasi fotokatalis α-Fe2O3/Bentonit pada plat kaca telah dilakukan dengan metode brush coating menggunakan double-sided adhesive tape (DSAT) sebagai perekat. Formulasi komposit α-Fe2O3/bentonit dibuat dengan mencampurkan α-Fe2O3 dan bentonit dengan perbandingan 3:1 (w/w). Aktivitas fotokatalitik fotokatalis α-Fe2O3/bentonit yang terimmobilisasi pada plat kaca dievaluasi pada penghilangan zat warna methylene blue (MB). Komposit α-Fe2O3/bentonit dan α-Fe2O3 dikarakterisasi menggunakan X-Ray Difrraction (XRD) untuk mengevaluasi struktur senyawa dan kristal dari komposit α-Fe2O3/bentonit dan α-Fe2O3. Morfologi permukaan fotokatalis α-Fe2O3/bentonit dikarakterisasi menggunakan Scanning Electron Microscope (SEM). Hasil penelitian menunjukkan bahwa aktivitas fotokatalis dalam mendegradasi zat warna MB terjadi pada massa fotokatalis optimum 40 mg, pH 5 dan konsentrasi zat warna 5 mg/L dengan nilai kinetika reaksi yang diperoleh sebesar 0,0843 menit-1 dan persen kehilangan (%R) yang diperoleh sebesar 98,60% selama 60 menit penyinaran dengan lampu fluorescent. Penggunaan kembali (reusabilitas) fotokatalis komposit α-Fe2O3/bentonit terhadap zat warna MB dilakukan sebanyak 5 kali dengan aktivitas fotokatalitik yang menurun seiring dengan pengulangan yang dilakukan yaitu 98,60 % hingga 94%.
Kata kunci : Immobilisasi, α-Fe2O3, bentonit, fotokatalis, methylene blue
Immobilization of α-Fe2O3/Bentonite photocatalyst on a glass plate was carried out with brush coating method using double-sided adhesive tape as a binder. Formulation of immobilization α-Fe2O3/Bentonite composite was made by mixing α-Fe2O3 and bentonite with mass ratio 3:1 (w/w). Photocatalytic activity of immobilized photocatalyst was evaluated on removal Methylene Blue (MB) dye. α-Fe2O3/Bentonite composite and α-Fe2O3/ are characterized using X-Ray Diffraction (XRD) to evaluated the compounds and crystal structures. Surface morphology of α-Fe2O3/Bentonite composite on a glass plat was characterized using Scanning Electron Microscope (SEM). The result showed that the photocatalytic activity at optimum conditions in degrading of MB dye was found at a photocatalyst mass of 40 mg, pH 5 and dye of concentration of 5 mg/L with the value of reaction kinetics obtained 0,0843 minutes-1 with percent loss of Methylene Blue dye (%R) obtained 98,60% during 60 minutes of irradiation with fluorescent lamps. Reusability of α-Fe2O3/Bentonite composite for degradation of MB dyes was carried out 5 cycles which gave decreased photocatalytic activity during repetition performed result were 98,60% for 94%. Key word : Immobilization, α-Fe2O3, bentonite, photocatalyst, methylene blue
DEGRADASI ZAT WARNA KATIONIK DAN ANIONIK MENGGUNAKAN IMMOBILISASI FOTOKATALIS TIO2/?-FE2O3/BENTONIT DIBAWAH LAMPU FLUORESCENCE (FERIZKA FRASTIWI, 2018)
FOTODEGRADASI ZAT WARNA INDIGO CARMINE MENGGUNAKAN KOMPOSIT ?-FE2O3 DARI BIJIH BESI/BENTONIT (Murisna, 2017)
FOTODEGRADASI ZAT WARNA INDIGO CARMINE MENGGUNAKAN FOTOKATALIS ?-FE2O3/BENTONIT (AFRI ALZAHRA, 2019)
AKTIFITAS FOTOKATALITIK KOMPOSIT TIO2-BENTONIT PADA DEGRADASI ZAT WARNA NAPTHOL BLUE BLACK (Novi Fadila, 2017)
PILARISASI BENTONIT TERAKTIVASI MENGGUNAKAN TIO2 DAN APLIKASINYA PADA DEGRADASI ZAT WARNA (Syahrinta Sepia Nika, 2016)