PENGARUH SUHU KALSINASI TERHADAP PREPARASI OKSIDA ANORGANIK DARI BATUAN MAGNESIT LOKAL ACEH DAN UJI AKTIVITAS KATALITIK PADA TRANSESTERIFIKASI MINYAK SAWIT (RBDPO)
Pengarang
Bahreina Adlin - Personal Name;
Dosen Pembimbing
Muliadi Ramli - 197303011998021001 - Dosen Pembimbing I
Sheilatina - 197808052003122001 - Dosen Pembimbing II
Nomor Pokok Mahasiswa
1908103010009
Fakultas & Prodi
Fakultas MIPA / Kimia (S1) / PDDIKTI : 47201
Subject
Kata Kunci
Penerbit
Banda Aceh : Fakultas mipa., 2023
Bahasa
No Classification
-
Literature Searching Service
Hard copy atau foto copy dari buku ini dapat diberikan dengan syarat ketentuan berlaku, jika berminat, silahkan hubungi via telegram (Chat Services LSS)
Penelitian pengaruh suhu kalsinasi pada proses preparasi katalis oksida anorganik dari batuan magnesit lokal Aceh menggunakan metode dekomposisi termal suhu tinggi telah berhasil dilakukan. Variasi suhu kalsinasi terhadap batuan magnesit (600ºC, 750ºC dan 900ºC) menyebabkan perubahan kandungan MgCO3 dalam batuan magnesit menjadi oksida magnesium. Hasil karakterisasi awal batuan magnesit lokal Aceh menunjukan kandungan magnesium karbonat (MgCO3) sebagai komponen utama dan sedikit pengotor yang terdiri dari CaCO3, Fe2O3 dan SiO2. Hasil penelitian juga mengkonfirmasi bahwa variasi suhu kalsinasi yang digunakan telah berpengaruh pada proses dekomposisi mineral magnesit menjadi oksida anorganik, sesuai hasil karakterisasi tentang sifat fisika-kimia yang menggunakan X-Ray Diffraction (XRD), Scanning Electron Microscope-Energy Dispersive Spectroscopy (SEM-EDS) dan Fourier Transform Infrared Spectroscopy (FTIRS). Katalis oksida anorganik hasil kalsinasi batuan magnesit lokal Aceh pada variasi suhu berbeda (600ºC, 750ºC dan 900ºC) telah diuji kinerja katalitiknya pada sistem reaksi transesterifikasi minyak sawit (RBDPO). Hasil transesterifikasi katalisis terhadap minyak RBDPO menunjukkan bahwa katalis oksida anorganik yang diperoleh pada kalsinasi pada 900ºC memiliki kinerja katalitik terbaik pada reaksi transesterifikasi RBDPO menjadi biodisel, dengan yield biodiesel sebesar 96,28%, sementara katalis oksida anorganik yang dipreparasi pada suhu kalsinasi 750ºC dan 600ºC masing-masing menghasilkan yield biodiesel sebesar 94,79% dan 92,13%.
Kata kunci: Suhu kalsinasi, magnesit lokal Aceh, transesterifikasi RBDPO, biodiesel
This research focused on the effect of calcination temperature for preparing inorganic oxide catalysts from local Aceh magnesite rock using high temperature thermal decomposition method. It had been confirmed that varying calcination temperature on magnesite rocks (600ºC, 750ºC and 900ºC) changed MgCO3 to magnesium oxide. The initial characterization of the local Aceh magnesite rock showed that it was consisted magnesium carbonate (MgCO3) as major component and a small amount of impurities consisted CaCO3, Fe2O3 and SiO2. This study also confirmed that varying calcination temperature has effected on the decomposition process of magnesite minerals into inorganic oxides, as it supported by characterization data using X-Ray Diffraction (XRD), Scanning Electron Microscope-Energy Dispersive Spectroscopy (SEM-EDS). and Fourier Transform Infrared Spectroscopy (FTIR). Finally, the inorganic oxide catalyst obtained at varied calcination temperature (600ºC, 750ºC and 900ºC) had been applied for catalytic performance in transesterification reaction of RBDPO oil, which indicated the application of inorganic oxide catalyst obtained at calcination at 900ºC had been best catalytic performance in resulting biodiesel, with a biodiesel yield of 96.28% compared to inorganic oxide catalyst obtained at 750ºC and 600ºC which were produced biodiesel yield of 94.79% and 92.13% respectively. Keywords: calcination temperature, Aceh local magnesite, RBDPO transesterification, biodiesel
PREPARASI KATALIS HETEROGEN ANORGANIK DARI BATUAN MAGNESIT LOKAL ACEH YANG TERMODIFIKASI LOGAM NATRIUM UNTUK SINTESIS BIODIESEL (Dea Kamara, 2023)
PEMANFAATAN MINERAL DOLOMIT LOKAL ACEH SEBAGAI KATALIS ANORGANIK UNTUK SINTESIS BIODIESEL (Minnati Rana Maisarah, 2021)
PREPARASAI KATALIS HETEROGEN ANORGANIK DARI BATUAN MAGNESIT LOKAL ACEH YANG TERMODIFIKASI DENGAN LOGAM KALIUM UNTUK SINTESIS BIODIESEL (Aya Sofia, 2023)
SINTESIS NANOPARTIKEL OKSIDA ANORGANIK DARI TULANG KERBAU ACEH (BUBALUS BUBALIS) UNTUK TRANSESTERIFIKASI MINYAK KELAPA SAWIT MENJADI BIODIESEL (Cut Putri Safira, 2024)
MODIFIKASI OKSIDA ANORGANIK DARI MINERAL KAOLIN ALAM JABOI SABANG SEBAGAI KATALIS HETEROGEN UNTUK SINTESIS BIODIESEL (ULFIRA RAHMATILLAH, 2023)