SKRIPSI
PENGARUH PENAMBAHAN SERAT POLYETHYLENE DENGAN VARIASI PANJANG SERAT TERHADAP RNKAPASITAS TARIK PELAT FERROFOAM CONCRETE
Pengarang
Minan Zuhri Zamia - Personal Name;
Dosen Pembimbing
Abdullah - 196403211989031002 - Dosen Pembimbing I
Nora Abdullah - 197307101998022003 - Dosen Pembimbing II
Nomor Pokok Mahasiswa
1904101010094
Fakultas & Prodi
Fakultas Teknik / Teknik Sipil (S1) / PDDIKTI : 22201
Subject
Kata Kunci
Penerbit
Banda Aceh : Fakultas Teknik., 2023
Bahasa
No Classification
-
Literature Searching Service
Hard copy atau foto copy dari buku ini dapat diberikan dengan syarat ketentuan berlaku, jika berminat, silahkan hubungi via telegram (Chat Services LSS)
Ferrocement adalah beton pracetak yang telah dikenal lama, namun
penggunaan mortar beton normal menghasilkan panel pracetak yang berat.
Penggunaan beton ringan seperti beton busa sebagai pengganti matriks pada
material ferrocement, disebut ferrofoam concrete, dapat mengatasi masalah ini.
Namun, beton busa memiliki kuat tarik rendah dan sifat getas, sehingga perlu
modifikasi seperti penambahan serat. Penelitian ini menguji kuat tarik pelat
ferrofoam concrete dengan matriks beton busa SG 1,4 dengan 10% tanah lempung
bentonit dan penambahan 0,5% serat polyethylene, variasi panjang 10 mm dan
15mm. Tujuannya mengidentifikasi pengaruh serat polyethylene dengan panjang
berbeda terhadap kapasitas tarik dan retak pelat ferrofoam concrete. Pengujian kuat
tekan dan tarik belah beton busa juga dilakukan. Benda uji yang digunakan berupa
pelat ferrofoam concrete 400 x 100 x 20 mm dengan 4 lapis wiremesh untuk
pengujian tarik pelat serta silinder 100 x 200 mm untuk pengujian kuat tekan dan
tarik belah beton busa. Metode pengujian mengacu pada standar ACI 549.1R-93
untuk ferrofoam concrete dan SNI 1974:2011 serta SNI 2401:2014 untuk beton
busa. Hasil Penelitian ini menunjukkan bahwa penambahan serat pada beton busa
dapat meningkatkan kapasitas tarik, serat lebih panjang memberikan hasil lebih
baik, kuat tarik belah beton berserat 15mm mencapai 13,84% kuat tekan beton.
Beton busa berserat 10mm dan tanpa serat memiliki rasio kuat tarik belah terhadap
kuat tekan 12,10% dan 11,54%. Penambahan serat juga meningkatkan kapasitas
retak pelat ferrofoam concrete, penambahan serat yang lebih panjang juga
menunjukkan peningkatan kapasitas retak yang lebih baik. Tegangan retak rata-rata
pelat tanpa serat 0,3 MPa, serat 10mm 0,9 MPa dan serat 15mm 1,5 MPa.
Ferrocement is a precast concrete that has been well-known for a long time; however, the use of normal concrete mortar results in heavy precast panels. The utilization of lightweight concrete, such as foam concrete, as a substitute for the matrix in ferrocement, termed as ferrofoam concrete, can overcome this issue. However, foam concrete possesses low tensile strength and brittle properties, necessitating modifications such as fiber addition. This study examines the tensile strength of ferrofoam concrete plates with a foam concrete matrix of SG 1.4 with 10% bentonite clay and the addition of 0.5% polyethylene fibers, with lengths of 10mm and 15mm. The aim is to identify the influence of different lengths of polyethylene fibers on the tensile capacity and crack behavior of ferrofoam concrete plates. Compressive and splitting tensile tests were also conducted on foam concrete. Test specimens included 400 x 100 x 20 mm ferrofoam concrete plates with 4 layers of wiremesh for the plate tensile test and 100 x 200 mm cylinders for foam concrete compressive and splitting tensile tests. Testing methods followed ACI 549.1R-93 standards for ferrofoam concrete and SNI 1974:2011 and SNI 2401:2014 standards for foam concrete. The results of this study indicate that fiber addition to foam concrete enhances its tensile capacity, with longer fibers yielding better results. Tensile splitting strength of 15mm fiber-reinforced foam concrete reached 13.84% of the compressive strength of concrete. Fiber-reinforced foam concrete with 10mm fibers and without fibers exhibited split tensile to compressive strength ratios of 12.10% and 11.54%, respectively. Fiber addition also increased the crack capacity of ferrofoam concrete plates, with longer fibers showing improved crack resistance. The average crack stress of plates without fibers was 0.3MPa, while those with 10mm and 15mm fibers were 0.9MPa and 1.5MPa, respectively.
KAPASITAS IMPACT PELAT FERROFOAM CONCRETE BERSERAT NILON DAN BERSERAT POLYPROPYLENE (FAKHRI HADI ALHAS, 2021)
KAPASITAS IMPACT PELAT FERROFOAM CONCRETE BERSERAT NYLON (Rahmad Syahputra, 2021)
KAPASITAS TARIK PELAT FERROFOAM CONCRETE DENGAN VARIASI TULANGAN WIREMESH (Nabila Fairuz, 2023)
KAPASITAS IMPACT PELAT FERROFOAM CONCRETE BERSERAT POLYPROPYLENE (MUHAMMAD RIZA FAHLEVI, 2021)
KAPASITAS IMPACT PELAT BETON BERTULANG MUTU TINGGI MENGGUNAKAN SERAT POLYPROPYLENE (M Nuril Khair, 2023)