ADSORPSI LOGAM FE DAN PB DALAM PELUMAS BEKAS MENGGUNAKAN NANOKOMPOSIT MONTMORILLONIT TERMODIFIKASI KITOSAN
Pengarang
RIZKA MAULIDANA - Personal Name;
Dosen Pembimbing
Julinawati - 197107011997022001 - Dosen Pembimbing I
Irfan Mustafa - 197411302002121001 - Dosen Pembimbing I
Nomor Pokok Mahasiswa
1608103010024
Fakultas & Prodi
Fakultas MIPA / Kimia (S1) / PDDIKTI : 47201
Subject
Kata Kunci
Penerbit
Banda Aceh : Fakultas MIPA Kimia., 2023
Bahasa
No Classification
-
Literature Searching Service
Hard copy atau foto copy dari buku ini dapat diberikan dengan syarat ketentuan berlaku, jika berminat, silahkan hubungi via telegram (Chat Services LSS)
ABSTRAK
Telah dilakukan modifikasi nanokomposit montmorillonit termodifikasi kitosan sebagai adsorben dalam menurunkan kadar logam Fe dan Pb dalam limbah pelumas bekas. Tujuan penelitian yaitu untuk mengetahui daya serap adsorben nanokomposit montmorillonit Aceh Utara pada kondisi optimum. Bentonit alam yang berasal dari Teupin Reusep Aceh Utara diisolasi menggunakan cara sedimentasi dan gelombang ultrasonic dengan daya 750 Watt pada suhu kamar sehingga membentuk nano montmorillonit. Karakterisasi bentonit, nano montmorillonit dan nanokomposit montmorillonit yang termodifikasi kitosan dilakukan dengan menggunakan XRF, PSA, FT-IR, XRD dan SEM dan AAS. Hasil karakterisasi PSA menunjukkan ukuran rata-rata MMT nanopartikel adalah sebesar 63,7 nm. Hasil FTIR menunjukkan MMT telah termodifikasi dengan kitosan yang dibuktikan dengan bergesernya beberapa bilangan gelombang dan adanya bilangan gelombang 3626.33 cm-1 yang menunjukkan adanya vibrasi ulur N-H, Hasil XRD menunjukkan MMT yang sudah dimodifikasi kitosan terlihat menjadi lebih amorf. Hasil SEM menunjukkan MMT termodifikasi kitosan memiliki morfologi lebih berpori dan rapat. Kondisi adsorpsi optimum untuk logam Fe maupun logam Pb yaitu terjadi pada massa yaitu 5 g dengan waktu kontak 240 menit. Efisiensi dan kapasitas logam Fe terhadap massa adsorben masing-masing diperoleh 53.17% dan 0,0011 mg/g, sedangkan untuk logam Pb, efisiensi adsorpsi diperoleh 59,43% dan kapasitas adsorpsinya 0,0004 mg/g. Persamaan isoterm adsorpsi logam Fe menggunakan adsorben montmorillonit termodifikasi kitosan mengikuti persamaan isoterm adsorpsi Langmuir dan isoterm adsorpsi Freundlich dengan nilai R2 masing-masing sebesar 0,99 dan 0,996 sedangkan untuk adsorpsi logam Pb mengikuti isoterm adsorpsi Freundlich dengan nilai R2 sebesar 0,991.
Kata kunci : Bentonit, Montmorillonit, Kitosan, Adsorpsi, Isoterm adsorpsi, Logam Fe, Logam Pb
ABSTRACT Modification of chitosan-modified montmorillonite nanocomposite has been carried out as an adsorbent in reducing Fe and Pb metal content in used lubricant waste. The research objective was to determine the absorption capacity of the North Aceh montmorillonite nanocomposite adsorbent at optimum conditions. Natural bentonite from Teupin Reusep, North Aceh, was isolated using sedimentation and ultrasonic waves with a power of 750 watts at room temperature to form nano montmorillonite. Characterization of bentonite, nano montmorillonite, and chitosan-modified montmorillonite nanocomposites was carried out using XRF, PSA, FT-IR, XRD and SEM, and AAS. The results of the PSA characterization showed that the average size of the MMT nanoparticles was 63.7 nm. FTIR results show that MMT has been modified with chitosan as evidenced by the shifting of several wave numbers and the presence of wave numbers of 3626.33 cm-1 which indicates the presence of N-H stretching vibrations. XRD results show that MMT which has been modified by chitosan appears to be more amorphous. The SEM results showed that the chitosan-modified MMT had a more porous and dense morphology Optimum adsorption conditions for Fe and Pb metals occurred at a mass of 5 g with a contact time of 240 minutes. The efficiency and capacity of Fe metal on adsorbent mass were 53.17% and 0.0011 mg/g respectively, while for Pb metal, the adsorption efficiency was 59.43% and the adsorption capacity was 0.0004 mg/g. The adsorption isotherm of Fe metal using chitosan-modified montmorillonite adsorbent follows the Langmuir adsorption isotherm and Freundlich adsorption isotherm with R2 values of 0.99 and 0.996 respectively, while for Pb metal adsorption follows the Freundlich adsorption isotherm with an R2 value of 0.991. Keywords: Bentonite, Montmorillonite, Chitosan, Adsorption, Adsorption Isotherm, Fe Metal, Pb Metal
MODIFIKASI MONTMORILLONIT ACEH UTARA DENGAN KITOSAN SEBAGAI ADSORBEN LOGAM MERKURI (HG) (Salasatun Nisa, 2023)
ADSORPSI LOGAM KADMIUM (CD) MENGGUNAKAN MONTMORILLONIT TERMODIFIKASI KARBON AKTIF CANGKANG KELAPA SAWIT (Sulastri, 2022)
PEMBUATAN KOMPOSIT KITOSAN-ARANG DAUN TERATAI SEBAGAI ADSORBEN LOGAM CD(II) (Riska Masrianti, 2018)
ADSORPSI LOGAM FE DAN MN MENGGUNAKAN ADSORBEN SELULOSA AMPAS BUAH MAHKOTA DEWA (PHALERIA MACROCARPA (SCHEFF.) BOERL.) YANG TERMODIFIKASI KITOSAN (Miftahul Azri, 2024)
PEMBUATAN DAN KARAKTERISASI KOMPOSIT KITOSAN-SELULOSA SEBAGAI ADSORBEN ION LOGAM CD(II) (SHABRINA, 2016)