Membran merupakan teknologi terbaru dalam pengolahan air. Membran komposit dikembangkan untuk menghilangkan kadar logam ion Cd2+ dalam air. Metode pembuatan membran ini adalah inversi fasa, yaitu proses sebuah polimer diubah secara terkendali dari fasa cair ke fasa padat. Komposisi membran terdiri dari 11% selulosa asetat, 20% formamida, 69% Aseton dan purolit dengan persen loading 0, 10, 20, 30 dan 40%. Hasil karakterisasi membran komposit (SA11%-P40%) memiliki derajat pengembangan sebesar 42,70%, porositas sebesar 33,61%, kuat tarik sebesar 4,74 kgf/mm2, elongasi sebesar 35,20% dan nilai fluks sebesar 92,52 L/m2jam. Hasil uji Fourier Transform Infra Red (FTIR) menunjukkan senyawa dengan gugus OH, C-H, C=O dan SO3-. Hasil pengujian diperoleh membran bekerja optimum pada waktu 10 menit dengan kapasitas adsorpsi 0,018 mg/g serta % penyerapan sebesar 82%. Hasil pengujian isoterm adsorpsi menunjukkan adsorpsi Cd2+ dengan menggunakan membran komposit mengikuti kaidah isoterm adsorpsi Langmuir dengan nilai R2=0,9869. Membran komposit setelah diregenerasi pertama dan kedua menggunakan NaCl 1 N dapat digunakan kembali untuk menurunkan ion Cd2+ dalam air sebesar 54% dan 35%. Pengujian membran komposit pada sampel Muara Sungai Krueng Aceh dan pada sampel aliran air Ie Suum yang mengandung Kadmiuum dapat menurunkan kadar Kadmium secara berturut-turut sebesar 0,0010 mg/L dan 0,0063 mg/L. Kandungan ion Cd2+ dalam sampel air Sungai Krueng Aceh dan Ie suum sudah memenuhi standar baku mutu. Membran komposit dapat menjadi metode alternatif dalam penurunan kadar ion Cd2+ dalam air.

Membranes are the latest technology in water treatment. Composite membranes were developed to remove metal levels of Cd2+ ions in water. The method of making this membrane is phase inversion, which is the process of a polymer being changed in a controlled manner from the liquid phase to the solid phase. The membrane composition consists of 11% cellulose acetate, 20% formamide, 69% acetone and purolite with percent loading 0, 10, 20, 30 and 40%. The composite membrane characterization results (SA11%-P40%) have a development degree of 42,70%, porosity of 3,61%, tensile strength of 4,74 kgf/mm2, elongation of 35,20% and flux value of 92,52 L/m2 hours. Fourier Transform Infra Red (FTIR) test results show compounds with OH, C-H, C=O and SO3- groups. The test results obtained the membrane worked optimally within 10 minutes with an adsorption capacity of 0.018 mg/g and an absorption % of 82%. The results of adsorption isotherms test show Cd2+ adsorption using a composite membrane following the Langmuir adsorption isotherm rule with a value of R2= 0,9869. Composite membranes after the first and second regeneration using NaCl 1 N can be reused to degrade Cd2+ ions in water by 54% and 35%. Composite membrane testing on samples of the Krueng Aceh River Estuary and on Ie Suum water flow samples containing Cadmiuum can reduce Cadmium levels by 0,001 mg/L and 0,0063 mg/L, respectively. The results showed that the content of Cd2+ ions in the water samples of the Krueng Aceh and Ie suum Rivers had met quality standards. Composite membranes can be an alternative method in reducing Cd2+ ion levels in water.